Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 8502 CLASSY GREY Heating aging the material 1000 hours at 125°C leads to a +7% change in the tensile strength, +4% change in elongation, and +12% change in tear strength. Ash is 15%. Multi-Flex TPE contains Krato.. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | (Condition L) ASTM D-1238-94a |
Multibase Multi-Flex® TPO DEFA 1047 The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238 |
Plaskolite Optix® CA-1000 I Clear High Impact Acrylic Resin High impact acrylic resin, injection molding gradeApplications: A high-impact acrylic resin for injection molding. This resin offers impact strengths up to ten times of general-purpose acrylic resi.. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
SABIC 318B Linear Low Density Polyethylene for Cast Film Product Description: 318B is a Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures u.. |
|||
Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Arkema Group Oroglas® HFI-10 Acrylic, Impact Grade
(discontinued **) OROGLAS HFI-10 is an impact grade that in addition to its superior impact resistance provides an improvement in flow which contribute to improve molding behavior and reduce cycle time.Key features :.. |
|||
Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
IRPC Polimaxx Polene 129PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP, ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
Kraton® D1102 + PP blend (10/90) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the .. |
|||
Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
IRPC Polimaxx Polene 320PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | (Condition I) ASTM D-1238-94a |
Multibase Multi-ABS 7522 R , 22% Filler Content Data provided by Multibase. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Borcoat™ MA115E Syntactic Polypropylene for Steel Pipe Coating Borcoat™ MA115E is a highly filled polypropylene compound and is self colored. Applications: Borcoat™ MA115E is recommended as heavy weight coating for special applications used in steel pipe coa.. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Bormed™ DM55pharm Polypropylene Bormed™ DM55pharm is a low melt flow rate polypropylene homopolymer intended for extrusion and thermoforming. Its very good organoleptic properties allows this grade to be used with any master bat.. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Bormod™ HC905TF Polypropylene Homopolymer for Thermoforming Bormod HC905TF is a low melt flow rate polypropylene homopolymer intended for thermoformed packaging applications. This homopolymer is produced using the Borealis Controlled Crystallinity Polypropy.. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
UBE UBEPOL B -B HIPS (Low-cis) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
UBE UBEPOL BR34HL HIPS (stirring rate = 500 rpm) Description: UBEPOL-BR34HL is characterized by its lower molecular weight and higher linear molecular chain compared with UBEPOL-BR15HB. The properties of HIPS modified by UBEPOL-BR34HL are very goo.. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis HC207TF Polypropylene Homopolymer HC207TF is a special nucleated polypropylene homopolymer intended for thermoforming packaging. Applications: HC207TF is recommended for in-line and off line thermoforming, high transparent trays, c.. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis HC600TF Polypropylene HC600TF is a polypropylene homopolymer intended for thermoformed packaging applications. Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring .. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 41E556 Anhydride-Modified LLDPE Adhesive Resin Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi.. |
|||
Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 H |
Total Polystyrene Impact 8260 Improved Environmental Stress Crack Resistance High Impact Polystyrene POLYSTYRENE IMPACT 8260 is a high impact polystyrene for extrusion and injection applications. This grade has an improved environmental stress crack resistance in comparison with standard high impa.. |
|||
Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
TPI Porene® AS 121 PC (Blue) General Purpose SAN Porene® is a registered trademark of Thai Petrochemical Industry Co. LTD. Information provided by Dayson Polymers. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ISO 1133 D |
Asahi Kasei Tenac® 3013A Homopolymer Acetal Resin Weather-Resistant grade containing UV absorber and other additives for superior weathering abilityInformation provided by Asahi Kasei Corporation. |
|||
Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Americas Styrenics STYRON® 484 High Impact Polystyrene Product CharacteristicsToughnessHeat resistanceGood stiffnessFood Contact CompliantUL Classification 94HBTypical ApplicationsLidsAppliances/RefrigerationPackaging/disposablesHousewaresInformation pr.. |
|||
Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Total PSI 975E Polystyrene Polystyrene 975E is a high impact polystyrene designed for extrusion/thermoforming applications. The food ESCR properties of 975E dictate its use for dairy applications that are subjected to high bu.. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | |
UBE A (High-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
Plaskolite West Optix® CP - 1000 I High Impact Acrylic Resin Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists g.. |
|||
Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238 |
E-Polymers EFLEX® I2040 Ionomer I-series (Ionomer): E-FLEX Ionomer is a family of ethylene acrylic acid (E/AA) copolymers, in which part of the acrylic acid is neutralized with metal ions such as zinc (Zn) or sodium (Na) or magnes.. |
|||
Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Arkema Group Oroglas® SG 10 Acrylic, Gamma Radiation Resistant
(discontinued **) OROGLAS SG 10 is special Gamma - radiation - resistant formulation designed for use in medical devises.OROGLAS SG 10 maintains exceptional clarity after 5 megarads of Gamma radiation with no advers.. |
|||
Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Arkema Group Oroglas® V 825 T Acrylic
(discontinued **) OROGLAS V 825 T exhibits an excellent balance of properties including superior thermal resistance with an easy processing behavior.OROGLAS V 825 T is then the material of choice for automotive appli.. |
|||
Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis Bormod™ HC904CF Polypropylene Bormod™ BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borstar® Nucleation Tech.. |