Solvay Technyl® C216V30 30% Glass Filled Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C216V30 30% Glass Filled Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % | 0.80 % | 24 Hr.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 175 MPa | 25400 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
| Flexural Strength | 240 MPa | 34800 psi | ASTM D790 |
| Flexural Modulus | 8.41 GPa | 1220 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 212 °C | 414 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Compression Zone |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Nozzle Temperature | 241 - 260 °C | 465 - 500 °F | |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 600 mm/sec | 7.87 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- Polimeri Europa EDISTIR PD RK4122H High Impact Polystyrene (HIPS) (discontinued **)
- Teijin Panlite® GS-3430 Friction and Abrasion Resistant, Glass Fiber Reinforced Polycarbonate Resin
- Solvay GEROPON® DA Surfactant
- A. Schulman POLYFORT™ PP 1930UX Extra High Flow, UV Stabilized Copolymer Polypropylene
- A. Schulman POLYBATCH™ Silver 7002/5 Concentrate Based In LDPE
- Hexcel® HexPly® F185 Epoxy Resin, K285 Kevlar Fabric
- Abatron 8509-4 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- DuPont Performance Polymers Zytel® 80G14A NC010A Nylon 66 (Unverified Data**)
- PolyOne Synprene® IT 39-020 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved