Eurostar Starflam RF0023E PA66/6, 10% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 10% Glass Fiber Reinforced
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam RF0023E PA66/6, 10% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam RF0023E is a Mineral Flame Retardant, Halogen Free and Phosphorous Free, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding (also known as RF1002Z230EM)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
ISO 1183
Water Absorption 0.80 %

@Temperature 23.0 °C,
Time 86400 sec
 0.80 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm

@Time 86400 sec
 0.0020 - 0.0050 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 94.0 MPa
13600 psi
ISO 527
Elongation at Break 1.5 - 2.5 %
1.5 - 2.5 %
ISO 527
Flexural Strength 132 MPa
19100 psi
ISO 178
Flexural Modulus 7.60 GPa
1100 ksi
ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 22.0 kJ/m²
10.5 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Thermal Conductivity 1.00 W/m-K
6.94 BTU-in/hr-ft²-°F
ASTM E1530
Hot Ball Pressure Test 178 °C

@Thickness 3.00 mm
 352 °F

@Thickness 0.118 in
 IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 178 °C
352 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
Vicat Softening Point 202 °C
396 °F
B/120; ISO 306
UL RTI, Electrical 130 °C

@Thickness 0.860 mm
 266 °F

@Thickness 0.0339 in
130 °C

@Thickness 1.70 mm
 266 °F

@Thickness 0.0669 in
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 105 °C

@Thickness 0.860 mm
 221 °F

@Thickness 0.0339 in
105 °C

@Thickness 1.70 mm
 221 °F

@Thickness 0.0669 in
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 120 °C

@Thickness 0.860 mm
 248 °F

@Thickness 0.0339 in
130 °C

@Thickness 1.70 mm
 266 °F

@Thickness 0.0669 in
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
Flammability, UL94 V-2

@Thickness 0.860 mm
 V-2

@Thickness 0.0339 in
 IEC 60695-11-10
V-0

@Thickness 1.70 mm
 V-0

@Thickness 0.0669 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.860 mm
 >= 120 sec

@Thickness 0.0339 in
 PLC 0
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.860 mm
 >= 120 arcs

@Thickness 0.0339 in
 PLC 0
>= 120 arcs

@Thickness 1.70 mm
 >= 120 arcs

@Thickness 0.0669 in
 PLC 0
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 270 - 280 °C
518 - 536 °F
Zone 1
Middle Barrel Temperature 275 - 285 °C
527 - 545 °F
Zone 2
Front Barrel Temperature 280 - 300 °C
536 - 572 °F
Zone 3
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %