Polymer Property : Flexural Strength = 132 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	132 MPa	19100 psi	ASTM D790
PolyOne Maxxam™ PPR-40G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Flexural Strength	132 MPa	19100 psi	ASTM D 790
SABIC Innovative Plastics Lexan® SP7604 PC (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	132 MPa	19100 psi
Cookson Group Plaskon® AMC2 (132.203) Epoxy Molding Compound (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound specifically formulated for packaging stress-sensitive devices in DIPs, SOICs, PLCCs and small QFPs. F..
Flexural Strength	132 MPa	19100 psi	ASTM D790
Kolon KOPAÂ® KN3322V0Y Flame Retardant Nylon 66 Halogen free, Impact -resistantApplications A variety of connectorsInformation provided by API-Kolon.
Flexural Strength	132 MPa	19100 psi	ASTM D790
Kotec Carbotex KG-15MRA Polycarbonate, 15% Glass Fiber Reinforced Features: Glass fiber 15% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Flexural Strength	132 MPa	19100 psi	ASTM D790
Kotec Carbotex KG-20F10 Polycarbonate, Wear Resistant, 20% Glass Fiber Reinforced Features: Glass fiber 20% reinforced, Mold release, Translucent, Dimensional stability, Non-frictionApplications: OA equipment, Communications, Precision parts, Machineries, E & E partsInformation p..
Flexural Strength	132 MPa	19100 psi	ASTM D790
Kotec Carbotex KGN-15MRA Polycarbonate, Flame Retardant, 15% Glass Fiber Reinforced Features: Glass fiber 15% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Flexural Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP UX06425 PPA LNP* LUBRICOMP* UX06425 is a compound based on Polyphthalamide (PPA) containing 10% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Hot Water Moldable and Heat Stab..
Flexural Strength	132 MPa	19200 psi	ASTM D790
Techmer ES ElectrablendÂ® ABS CF10 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightFeatures: Flame RetardantAppearance: BlackInformation provided by TP Composites, Inc.
Flexural Strength	132 MPa	19100 psi	ASTM D 790
SABIC Innovative Plastics LNP Lubriloy DF202 PC LNP LUBRILOY* DF202 is a compound based on Polycarbonate resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied b..
Flexural Strength	132 MPa	19100 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRILOY DF202P PC LNP LUBRILOY* DF202P is a compound based on Polycarbonate resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Exceptional Processing.
Flexural Strength	132 MPa	19100 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON DDF029 PC (Asia Pacific) LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant, Glass Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON EX11402 PEI LNP* STAT-KON* EX11402 is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Flexural Strength	132 MPa	19100 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC (Asia Pacific) LNP* THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing Glass Fiber, Milled Glass. Added features of this material include: Exceptional Processing.
Flexural Strength	132 MPa	19100 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Lexan_SP7604 PC (Asia Pacific)
Flexural Strength	132 MPa	19100 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 136F4Q32 Nylon 6, 20% Glass Fiber SAXAMID 136F4Q32 is a high impact-modified polyamide 6 injection-molding-grade reinforced with 20% glass fibers.Information provided by SAX Polymers
Flexural Strength	132 MPa	19100 psi	ASTM D790
SABIC Innovative Plastics NORYL HFG300 PPE+PS (Asia Pacific) PPE+PS GF30% filled, FR V-0
Flexural Strength	132 MPa	19100 psi	ASTM D790
SABIC Innovative Plastics NORYL NC220 PPE+HIPS (Asia Pacific)
Flexural Strength	132 MPa	19100 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON DDF029 PC LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant.
Flexural Strength	132 MPa	19100 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC LNP THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Exceptional Processing.
Flexural Strength	132 MPa	19100 psi	ASTM D790
Teknor Apex Sinpolene GPP1640 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 40% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; ..
Flexural Strength	132 MPa	19200 psi	ASTM D790
Chase Plastics CP Pryme® N340HSL (COND, 50% RH) Nylon 6 (Utility Grade), 40% Glass Fiber Reinforced, Heat Stabilized, Internally Lubricated Information provided by Chase Plastics.
Flexural Strength	132 MPa	19200 psi	ASTM D790
Ensinger Tecapeek® XP-181 Compression Molded PPEK Compound, EWS Filled and Carbon Fiber Reinforced Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Flexural Strength	132 MPa	19100 psi	ISO 178
DuPont Performance Polymers Rynite® 935 BK505 Polyethylene Terephthalate (PET) (Unverified Data**) 35% Glass Reinforced Polyethylene Terephthalate Rynite 935 BK505 is a 35% mica/glass reinforced modified polyethylene terephthalate resin with exceptionally low warpage excellent electrical properti..
Flexural Strength	132 MPa	19100 psi	ISO 178
Eurostar Starflam RF0023E PA66/6, 10% Glass Filled, Injection Molded Starflam RF0023E is a Mineral Flame Retardant, Halogen Free and Phosphorous Free, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding (also known as RF1002Z230EM)Information provided by Polymer..
Flexural Strength	132 MPa	19100 psi	Machine; IPC TM-650 2.4.4
Arlon CLTE Microwave Printed Circuit Board Substrate CLTE is a ceramic powder-filled and woven micro fiberglass reinforced PTFE composite engineered to produce a stable, low water absorption laminate with a nominal Dielectric Constant of 2.98.Ceramic/..