Eastman DuraStar DS1000 Polymer, Natural

Category Polymer , Thermoplastic , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT) , Glycol-Modified PCT (PCTG) Copolyester
Manufacturer Eastman Chemical
Trade Name DuraStar
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman DuraStar DS1000 Polymer, Natural.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Durastar DS1000 polymer has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS1000 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily, fills intricate molds, and is well suited for thick-wall applications. Under existing United States Food and Drug Administration (FDA) regulations, Durastar DS1000 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240.Applications/UsesFloor careHousewaresToys/Sporting goodsFurniture/Furniture trimPoint of purchase displaysWriting instrumentsKey AttributesGood chemical resistanceExcellent flowOutstanding impact resistanceExcellent clarityFast drying timesQuick cycle times
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0060 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 103
103
ASTM D785
Tensile Strength at Break 46.0 MPa
6670 psi
ISO 527
51.0 MPa
7400 psi
ASTM D638
Tensile Strength, Yield 47.0 MPa
6820 psi
ASTM D638
47.0 MPa
6820 psi
ISO 527
Elongation at Break 200 %
200 %
ISO 527
300 %
300 %
ASTM D638
Elongation at Yield 4.0 %
4.0 %
ISO 527
5.0 %
5.0 %
ASTM D638
Tensile Modulus 1.80 GPa
261 ksi
ISO 527
Flexural Strength 65.0 MPa
9430 psi
ISO 178
Flexural Yield Strength 69.0 MPa
10000 psi
ASTM D790
Flexural Modulus 1.85 GPa
268 ksi
ISO 178
2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 0.400 J/cm

@Temperature -40.0 °C
0.749 ft-lb/in

@Temperature -40.0 °F
ASTM D256
0.800 J/cm

@Temperature 23.0 °C
1.50 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 4.80 kJ/m²

@Temperature -40.0 °C
2.28 ft-lb/in²

@Temperature -40.0 °F
ISO 180
7.80 kJ/m²

@Temperature 23.0 °C
3.71 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Puncture Energy 42.0 J
31.0 ft-lb
Puncture Resistance @Max Load, 23°C; ASTM D3763
58.7 J
43.3 ft-lb
Puncture Resistance @ max load, 23°C; ISO 6603-2
48.0 J

@Temperature -40.0 °C
35.4 ft-lb

@Temperature -40.0 °F
Puncture Resistance at Max Load; ASTM D3763
52.6 J

@Temperature -40.0 °C
38.8 ft-lb

@Temperature -40.0 °F
Puncture Resistance at Max Load; ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 72.0 °C
162 °F
ISO 75
75.0 °C
167 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ASTM D648
66.0 °C
151 °F
ISO 75
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Optical Properties Metric English Comments
Haze 0.30 %
0.30 %
ASTM D1003
Transmission, Visible 89 %
89 %
Regular Transmittance; ASTM D1003
91 %
91 %
Total Transmittance; ASTM D1003
Processing Properties Metric English Comments
Melt Temperature 230 - 280 °C
446 - 536 °F
Mold Temperature 15.0 - 30.0 °C
59.0 - 86.0 °F
Drying Temperature 70.0 °C
158 °F
Dry Time 3 hour
3 hour