DuPont™ Tedlar® SP TXX10AH9 Polyvinyl Fluoride Film

Category Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer DuPont
Trade Name Tedlar® SP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Tedlar® SP TXX10AH9 Polyvinyl Fluoride Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Colored, High Gloss. Tedlar® SP polyvinyl fluoride film is designed to provide excellent conformability to substrates while maintaining the superb durability, color stability, chemical resistance, and ease of cleaning expected of PVF film. Tedlar® SP also offers custom color capability not previously available in PVF film. Tedlar® SP is an unoriented film. It possesses high elongation and moderate yield stress. After lamination using conventional means, it can be easily embossed and will maintain high pattern definition. Tedlar® SP can also be subjected to high levels of forming without significant recovery stresses.Information provided by DuPont.
Physical Properties Metric English Comments
Thickness 25.4 microns
1.00 mil
Mechanical Properties Metric English Comments
Tensile Strength 13.0 - 17.0 MPa

@Temperature 100 °C
1890 - 2470 psi

@Temperature 212 °F
20.0 - 24.0 MPa

@Temperature 75.0 °C
2900 - 3480 psi

@Temperature 167 °F
26.0 - 30.0 MPa

@Temperature 50.0 °C
3770 - 4350 psi

@Temperature 122 °F
34.0 - 43.0 MPa

@Temperature 20.0 °C
4930 - 6240 psi

@Temperature 68.0 °F
ASTM D882-80, Method A - 100%
Elongation at Break 100 %
100 %
ASTM D882-80
Tear Strength 550 kN/m
3140 pli
Graves, MD; ASTM D1004
550 kN/m
3140 pli
Graves, TD; ASTM D1004
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 107 °C
225 °F
Continuous
175 °C
347 °F
Short Cycle
Minimum Service Temperature, Air -72.0 °C
-97.6 °F
Continuous
Shrinkage <= 2.0 %

@Temperature 170 °C
<= 2.0 %

@Temperature 338 °F
ASTM D1204-78
0.60 %

@Temperature 50.0 °C,
Time 1800 sec
0.60 %

@Temperature 122 °F,
Time 0.500 hour
1.2 %

@Temperature 100 °C,
Time 1800 sec
1.2 %

@Temperature 212 °F,
Time 0.500 hour
1.6 %

@Temperature 150 °C,
Time 1800 sec
1.6 %

@Temperature 302 °F,
Time 0.500 hour
Optical Properties Metric English Comments
Gloss 57 %
57 %
20°; Gardner
81 %
81 %
60°; Gardner
93 %
93 %
85°; Gardner
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+13 ohm-cm
4.00e+13 ohm-cm
ASTM D257-78
Dielectric Constant 7.0
7.0
ASTM D151-81
Dielectric Strength 118 kV/mm
3000 kV/in
ASTM D151-81
Dissipation Factor 0.0020
0.0020
ASTM D151-81
Processing Properties Metric English Comments
Processing Temperature 105 - 171 °C
221 - 340 °F
Film Forming Surface Temperature
Descriptive Properties Value Comments
Resistance to Acids No Visible Effect
2 hr Boiling
Resistance to Bases No Visible Effect
Immersion
Weatherability Excellent