DuPont Performance Polymers Zytel® ST801AW BK195 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® ST801AW BK195 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® ST801AW BK195 is a Super Tough, weatherable, easy flow and processing friendly, black polyamide 66 resin for injection molding. It offers the best resistance to outdoor exposure.Information provided by DuPont
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
DAM; ISO 1183
Water Absorption 1.07 %

@Temperature 23.0 °C
 1.07 %

@Temperature 73.4 °F
 DAM; Immersion 24h; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.022 cm/cm

@Thickness 2.00 mm
 0.022 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.020 cm/cm

@Thickness 2.00 mm
 0.020 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 23.0 °C
 6530 psi

@Temperature 73.4 °F
 DAM; 50mm/min; ISO 527
Tensile Stress 41.0 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 5950 psi

@Strain 50.0 %,
Temperature 73.4 °F
 50%RH; ISO 527
50.0 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 7250 psi

@Strain 50.0 %,
Temperature 73.4 °F
 DAM; ISO 527
Tensile Strength, Yield 47.0 MPa

@Temperature 23.0 °C
 6820 psi

@Temperature 73.4 °F
 DAM; ISO 527
Elongation at Break 48 %

@Temperature 23.0 °C
 48 %

@Temperature 73.4 °F
 DAM; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50%RH; ISO 527
75 %

@Temperature 23.0 °C
 75 %

@Temperature 73.4 °F
 DAM; 50mm/min; ISO 527
Elongation at Yield 30 %

@Temperature 23.0 °C
 30 %

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Modulus 1.237 GPa

@Temperature 23.0 °C
 179.4 ksi

@Temperature 73.4 °F
 50%RH; ISO 527
1.90 GPa

@Temperature 23.0 °C
 276 ksi

@Temperature 73.4 °F
 DAM; ISO 527
Flexural Modulus 1.80 GPa

@Temperature 23.0 °C
 261 ksi

@Temperature 73.4 °F
 DAM; ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²

@Temperature -40.0 °C
 8.57 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
76.0 kJ/m²

@Temperature 23.0 °C
 36.2 ft-lb/in²

@Temperature 73.4 °F
 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 DAM; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 DAM; ISO 179/1eU
Charpy Impact, Notched 1.90 J/cm²

@Temperature -40.0 °C
 9.04 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eA
7.90 J/cm²

@Temperature 23.0 °C
 37.6 ft-lb/in²

@Temperature 73.4 °F
 DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature -40.0 - 23.0 °C
 61.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ASTM E 831
110 µm/m-°C

@Temperature -40.0 - 23.0 °C
 61.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ISO 11359-1/-2
120 µm/m-°C

@Temperature -30.0 - 30.0 °C
 66.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ASTM E 831
120 µm/m-°C

@Temperature -30.0 - 30.0 °C
 66.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ISO 11359-1/-2
150 µm/m-°C

@Temperature 55.0 - 160 °C
 83.3 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ISO 11359-1/-2
150 µm/m-°C

@Temperature 55.0 - 160 °C
 83.3 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ASTM E 831
150 µm/m-°C

@Temperature 23.0 - 55.0 °C
 83.3 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ISO 11359-1/-2
150 µm/m-°C

@Temperature 23.0 - 55.0 °C
 83.3 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ASTM E 831
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature -40.0 - 23.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ASTM E 831
100 µm/m-°C

@Temperature -40.0 - 23.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ISO 11359-1/-2
110 µm/m-°C

@Temperature -30.0 - 30.0 °C
 61.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ASTM E 831
110 µm/m-°C

@Temperature -30.0 - 30.0 °C
 61.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ISO 11359-1/-2
130 µm/m-°C

@Temperature 55.0 - 160 °C
 72.2 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ASTM E 831
130 µm/m-°C

@Temperature 23.0 - 55.0 °C
 72.2 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ISO 11359-1/-2
130 µm/m-°C

@Temperature 55.0 - 160 °C
 72.2 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ISO 11359-1/-2
130 µm/m-°C

@Temperature 23.0 - 55.0 °C
 72.2 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ASTM E 831
Melting Point 262 °C
504 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 162 °C
324 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 62.0 °C
144 °F
DAM; ISO 75-1/-2
UL RTI, Electrical 125 °C

@Thickness 0.750 mm
 257 °F

@Thickness 0.0295 in
 DAM; UL 746B
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.750 mm
 167 °F

@Thickness 0.0295 in
 DAM; UL 746B
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.750 mm
 185 °F

@Thickness 0.0295 in
 DAM; UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 DAM; IEC 60695-11-10
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 DAM; UL94
Electrical Properties Metric English Comments
Volume Resistivity 7.40e+12 ohm-cm

@Temperature 23.0 °C
 7.40e+12 ohm-cm

@Temperature 73.4 °F
 50%RH; IEC 60093
2.00e+16 ohm-cm

@Temperature 23.0 °C
 2.00e+16 ohm-cm

@Temperature 73.4 °F
 DAM; IEC 60093
Surface Resistance 3.00e+12 ohm

@Temperature 23.0 °C
 3.00e+12 ohm

@Temperature 73.4 °F
 50%RH; IEC 60093
2.40e+16 ohm

@Temperature 23.0 °C
 2.40e+16 ohm

@Temperature 73.4 °F
 DAM; IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.7

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
3.9

@Frequency 100 Hz,
Temperature 23.0 °C
 3.9

@Frequency 100 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
4.0

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 4.0

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
6.7

@Frequency 100 Hz,
Temperature 23.0 °C
 6.7

@Frequency 100 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
Dielectric Strength 22.0 kV/mm

@Temperature 23.0 °C
 559 kV/in

@Temperature 73.4 °F
 50%RH; IEC 60243-1
25.0 kV/mm

@Temperature 23.0 °C
 635 kV/in

@Temperature 73.4 °F
 DAM; IEC 60243-1
Dissipation Factor 0.0060

@Frequency 100 Hz,
Temperature 23.0 °C
 0.0060

@Frequency 100 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
0.012

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.012

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
0.044

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.044

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
0.159

@Frequency 100 Hz,
Temperature 23.0 °C
 0.159

@Frequency 100 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
Comparative Tracking Index 600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 DAM; IEC 60112
600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 DAM; UL 746A
Processing Properties Metric English Comments
Melt Temperature 270 - 300 °C
518 - 572 °F
DAM
290 °C
554 °F
DAM; optimum
Mold Temperature 70.0 °C
158 °F
DAM; Optimum
50.0 - 90.0 °C
122 - 194 °F
DAM
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM; Dehumidified Dryer