DuPont Performance Polymers Zytel® RS LC1600 NC010 Nylon 1010

Category Polymer , Thermoplastic , Nylon
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS LC1600 NC010 Nylon 1010.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plasticized Toughened UV Stabilized Renewably Sourced Polyamide 1010 Developed for Extrusion Zytel RS LC1600 NC010 is a renewable sourced Polyamide 1010 containing a minimum of 60% renewably sourced ingredient by weight. It is flexible toughened and plInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
DAM; ISO 1183
Viscosity 260000 cP

@Temperature 250 °C
 260000 cP

@Temperature 482 °F
 DAM; @ 1000 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.026 cm/cm
0.026 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 27.0 MPa

@Strain 50.0 %
 3920 psi

@Strain 50.0 %
 50%RH; ISO 527-1/-2
29.0 MPa

@Strain 50.0 %
 4210 psi

@Strain 50.0 %
 DAM; ISO 527-1/-2
0.900 MPa

@Strain 0.240 %,
Temperature 40.0 °C
 131 psi

@Strain 0.240 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.960 MPa

@Strain 0.250 %,
Temperature 40.0 °C
 139 psi

@Strain 0.250 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
1.26 MPa

@Strain 0.240 %,
Temperature 23.0 °C
 183 psi

@Strain 0.240 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.42 MPa

@Strain 0.190 %,
Temperature 23.0 °C
 206 psi

@Strain 0.190 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
1.93 MPa

@Strain 0.910 %,
Temperature 90.0 °C
 280 psi

@Strain 0.910 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
2.08 MPa

@Strain 0.180 %,
Temperature 0.000 °C
 302 psi

@Strain 0.180 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
2.23 MPa

@Strain 0.180 %,
Temperature 0.000 °C
 323 psi

@Strain 0.180 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
3.28 MPa

@Strain 4.15 %,
Temperature 150 °C
 476 psi

@Strain 4.15 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3.45 MPa

@Strain 4.11 %,
Temperature 150 °C
 500 psi

@Strain 4.11 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
5.26 MPa

@Strain 2.77 %,
Temperature 90.0 °C
 763 psi

@Strain 2.77 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
7.22 MPa

@Strain 50.0 %,
Temperature 150 °C
 1050 psi

@Strain 50.0 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
7.56 MPa

@Strain 50.0 %,
Temperature 150 °C
 1100 psi

@Strain 50.0 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.93 MPa

@Strain 31.42 %,
Temperature 90.0 °C
 1875 psi

@Strain 31.42 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
13.94 MPa

@Strain 39.63 %,
Temperature 90.0 °C
 2022 psi

@Strain 39.63 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
18.75 MPa

@Strain 0.790 %,
Temperature -40.0 °C
 2719 psi

@Strain 0.790 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
20.91 MPa

@Strain 33.17 %,
Temperature 40.0 °C
 3033 psi

@Strain 33.17 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
22.16 MPa

@Strain 34.18 %,
Temperature 40.0 °C
 3214 psi

@Strain 34.18 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
23.41 MPa

@Strain 1.47 %,
Temperature -20.0 °C
 3395 psi

@Strain 1.47 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
24.52 MPa

@Strain 1.09 %,
Temperature -40.0 °C
 3556 psi

@Strain 1.09 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
26.31 MPa

@Strain 34.51 %,
Temperature 23.0 °C
 3816 psi

@Strain 34.51 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
29.71 MPa

@Strain 26.46 %,
Temperature 23.0 °C
 4309 psi

@Strain 26.46 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
35.0 MPa

@Strain 13.0 %,
Temperature 0.000 °C
 5080 psi

@Strain 13.0 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
39.77 MPa

@Strain 2.88 %,
Temperature -20.0 °C
 5768 psi

@Strain 2.88 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
41.0 MPa

@Strain 15.0 %,
Temperature 0.000 °C
 5950 psi

@Strain 15.0 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
51.34 MPa

@Strain 10.19 %,
Temperature -20.0 °C
 7446 psi

@Strain 10.19 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
53.85 MPa

@Strain 12.08 %,
Temperature -20.0 °C
 7810 psi

@Strain 12.08 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
65.89 MPa

@Strain 4.72 %,
Temperature -40.0 °C
 9557 psi

@Strain 4.72 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
66.65 MPa

@Strain 4.56 %,
Temperature -40.0 °C
 9667 psi

@Strain 4.56 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
73.74 MPa

@Strain 9.47 %,
Temperature -40.0 °C
 10700 psi

@Strain 9.47 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
74.67 MPa

@Strain 9.53 %,
Temperature -40.0 °C
 10830 psi

@Strain 9.53 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Elongation at Break >= 50 %
>= 50 %
DAM; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; ISO 527-1/-2
200 %
200 %
DAM; 50mm/min; ISO 527-1/-2
200 %
200 %
50%RH; 50mm/min; ISO 527-1/-2
Tensile Modulus 0.420 GPa
60.9 ksi
50%RH; ISO 527-1/-2
0.590 GPa
85.6 ksi
DAM; ISO 527-1/-2
0.149 GPa

@Temperature 120 °C
 21.6 ksi

@Temperature 248 °F
 50%RH; ISO 11403-1 -2
0.150 GPa

@Temperature 120 °C
 21.8 ksi

@Temperature 248 °F
 DAM; ISO 11403-1 -2
0.355 GPa

@Temperature 40.0 °C
 51.5 ksi

@Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.376 GPa

@Temperature 40.0 °C
 54.5 ksi

@Temperature 104 °F
 DAM; ISO 11403-1 -2
2.128 GPa

@Temperature -40.0 °C
 308.6 ksi

@Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.443 GPa

@Temperature -40.0 °C
 354.3 ksi

@Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Secant Modulus 0.0648 GPa

@Strain 34.18 %,
Temperature 40.0 °C
 9.40 ksi

@Strain 34.18 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.0762 GPa

@Strain 34.51 %,
Temperature 23.0 °C
 11.1 ksi

@Strain 34.51 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.269 GPa

@Strain 13.0 %,
Temperature 0.000 °C
 39.0 ksi

@Strain 13.0 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
0.273 GPa

@Strain 15.0 %,
Temperature 0.000 °C
 39.6 ksi

@Strain 15.0 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
0.375 GPa

@Strain 0.240 %,
Temperature 40.0 °C
 54.4 ksi

@Strain 0.240 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.384 GPa

@Strain 0.250 %,
Temperature 40.0 °C
 55.7 ksi

@Strain 0.250 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.504 GPa

@Strain 10.19 %,
Temperature -20.0 °C
 73.1 ksi

@Strain 10.19 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
0.525 GPa

@Strain 0.240 %,
Temperature 23.0 °C
 76.1 ksi

@Strain 0.240 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.747 GPa

@Strain 0.190 %,
Temperature 23.0 °C
 108 ksi

@Strain 0.190 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
1.16 GPa

@Strain 0.180 %,
Temperature 0.000 °C
 168 ksi

@Strain 0.180 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
1.24 GPa

@Strain 0.180 %,
Temperature 0.000 °C
 180 ksi

@Strain 0.180 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
1.3809 GPa

@Strain 2.88 %,
Temperature -20.0 °C
 200.29 ksi

@Strain 2.88 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
1.40 GPa

@Strain 4.72 %,
Temperature -40.0 °C
 202 ksi

@Strain 4.72 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
1.46 GPa

@Strain 4.56 %,
Temperature -40.0 °C
 212 ksi

@Strain 4.56 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
1.59 GPa

@Strain 1.47 %,
Temperature -20.0 °C
 231 ksi

@Strain 1.47 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
2.25 GPa

@Strain 1.09 %,
Temperature -40.0 °C
 326 ksi

@Strain 1.09 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.37 GPa

@Strain 0.790 %,
Temperature -40.0 °C
 344 ksi

@Strain 0.790 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Charpy Impact Unnotched NB
NB
DAM; ISO 179/1eU