DuPont Performance Polymers Rynite® GW520CS NC010 Polyethylene Terephthalate (PET)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® GW520CS NC010 Polyethylene Terephthalate (PET).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced Flame Retardant Polyethylene Terephthalate with Improved Glow Wire Performance Rynite GW520CS NC010 is a 20% glass fiber reinforced flame retardant color stabilized modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ISO 1183
Melt Flow 17 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 17 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
ISO 527-1/-2
Tensile Stress 6.65 MPa

@Strain 0.190 %,
Temperature 150 °C
 965 psi

@Strain 0.190 %,
Temperature 302 °F
 ISO 11403-1 -2
11.36 MPa

@Strain 0.230 %,
Temperature 90.0 °C
 1648 psi

@Strain 0.230 %,
Temperature 194 °F
 ISO 11403-1 -2
30.76 MPa

@Strain 1.22 %,
Temperature 150 °C
 4461 psi

@Strain 1.22 %,
Temperature 302 °F
 ISO 11403-1 -2
34.55 MPa

@Strain 0.790 %,
Temperature 90.0 °C
 5011 psi

@Strain 0.790 %,
Temperature 194 °F
 ISO 11403-1 -2
42.36 MPa

@Strain 0.520 %,
Temperature 40.0 °C
 6144 psi

@Strain 0.520 %,
Temperature 104 °F
 ISO 11403-1 -2
43.13 MPa

@Strain 2.19 %,
Temperature 150 °C
 6255 psi

@Strain 2.19 %,
Temperature 302 °F
 ISO 11403-1 -2
51.11 MPa

@Strain 3.27 %,
Temperature 150 °C
 7413 psi

@Strain 3.27 %,
Temperature 302 °F
 ISO 11403-1 -2
52.15 MPa

@Strain 1.35 %,
Temperature 90.0 °C
 7564 psi

@Strain 1.35 %,
Temperature 194 °F
 ISO 11403-1 -2
60.93 MPa

@Strain 7.09 %,
Temperature 150 °C
 8837 psi

@Strain 7.09 %,
Temperature 302 °F
 ISO 11403-1 -2
66.32 MPa

@Strain 0.770 %,
Temperature 23.0 °C
 9619 psi

@Strain 0.770 %,
Temperature 73.4 °F
 ISO 11403-1 -2
66.64 MPa

@Strain 1.97 %,
Temperature 90.0 °C
 9665 psi

@Strain 1.97 %,
Temperature 194 °F
 ISO 11403-1 -2
68.3 MPa

@Strain 0.900 %,
Temperature 40.0 °C
 9910 psi

@Strain 0.900 %,
Temperature 104 °F
 ISO 11403-1 -2
77.0 MPa

@Strain 0.860 %,
Temperature -20.0 °C
 11200 psi

@Strain 0.860 %,
Temperature -4.00 °F
 ISO 11403-1 -2
77.04 MPa

@Strain 0.880 %,
Temperature 0.000 °C
 11170 psi

@Strain 0.880 %,
Temperature 32.0 °F
 ISO 11403-1 -2
91.1 MPa

@Strain 1.32 %,
Temperature 40.0 °C
 13200 psi

@Strain 1.32 %,
Temperature 104 °F
 ISO 11403-1 -2
101.52 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 14724 psi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
108.6 MPa

@Strain 1.76 %,
Temperature 40.0 °C
 15750 psi

@Strain 1.76 %,
Temperature 104 °F
 ISO 11403-1 -2
121.11 MPa

@Strain 1.73 %,
Temperature 23.0 °C
 17566 psi

@Strain 1.73 %,
Temperature 73.4 °F
 ISO 11403-1 -2
123.93 MPa

@Strain 1.55 %,
Temperature 0.000 °C
 17975 psi

@Strain 1.55 %,
Temperature 32.0 °F
 ISO 11403-1 -2
133.42 MPa

@Strain 1.65 %,
Temperature -20.0 °C
 19351 psi

@Strain 1.65 %,
Temperature -4.00 °F
 ISO 11403-1 -2
142.03 MPa

@Strain 2.35 %,
Temperature 23.0 °C
 20600 psi

@Strain 2.35 %,
Temperature 73.4 °F
 ISO 11403-1 -2
145.58 MPa

@Strain 1.98 %,
Temperature 0.000 °C
 21115 psi

@Strain 1.98 %,
Temperature 32.0 °F
 ISO 11403-1 -2
157.63 MPa

@Strain 2.10 %,
Temperature -20.0 °C
 22862 psi

@Strain 2.10 %,
Temperature -4.00 °F
 ISO 11403-1 -2
167.5 MPa

@Strain 2.61 %,
Temperature 0.000 °C
 24290 psi

@Strain 2.61 %,
Temperature 32.0 °F
 ISO 11403-1 -2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 9.00 GPa
1310 ksi
ISO 527-1/-2
3.013 GPa

@Temperature 150 °C
 437.0 ksi

@Temperature 302 °F
 ISO 11403-1 -2
6.316 GPa

@Temperature 60.0 °C
 916.1 ksi

@Temperature 140 °F
 ISO 11403-1 -2
9.165 GPa

@Temperature -20.0 °C
 1329 ksi

@Temperature -4.00 °F
 ISO 11403-1 -2
Secant Modulus 4.66 GPa

@Strain 2.83 %,
Temperature 40.0 °C
 675 ksi

@Strain 2.83 %,
Temperature 104 °F
 ISO 11403-1 -2
5.52 GPa

@Strain 2.72 %,
Temperature 23.0 °C
 801 ksi

@Strain 2.72 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.72 GPa

@Strain 2.07 %,
Temperature 40.0 °C
 829 ksi

@Strain 2.07 %,
Temperature 104 °F
 ISO 11403-1 -2
6.51 GPa

@Strain 2.03 %,
Temperature 23.0 °C
 945 ksi

@Strain 2.03 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.61 GPa

@Strain 1.48 %,
Temperature 40.0 °C
 959 ksi

@Strain 1.48 %,
Temperature 104 °F
 ISO 11403-1 -2
7.12 GPa

@Strain 2.13 %,
Temperature 0.000 °C
 1030 ksi

@Strain 2.13 %,
Temperature 32.0 °F
 ISO 11403-1 -2
7.29 GPa

@Strain 2.26 %,
Temperature -20.0 °C
 1060 ksi

@Strain 2.26 %,
Temperature -4.00 °F
 ISO 11403-1 -2
7.59 GPa

@Strain 0.900 %,
Temperature 40.0 °C
 1100 ksi

@Strain 0.900 %,
Temperature 104 °F
 ISO 11403-1 -2
7.81 GPa

@Strain 1.30 %,
Temperature 23.0 °C
 1130 ksi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.00 GPa

@Strain 1.55 %,
Temperature 0.000 °C
 1160 ksi

@Strain 1.55 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.09 GPa

@Strain 1.65 %,
Temperature -20.0 °C
 1170 ksi

@Strain 1.65 %,
Temperature -4.00 °F
 ISO 11403-1 -2
8.15 GPa

@Strain 0.520 %,
Temperature 40.0 °C
 1180 ksi

@Strain 0.520 %,
Temperature 104 °F
 ISO 11403-1 -2
8.61 GPa

@Strain 0.770 %,
Temperature 23.0 °C
 1250 ksi

@Strain 0.770 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.75 GPa

@Strain 0.880 %,
Temperature 0.000 °C
 1270 ksi

@Strain 0.880 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.95 GPa

@Strain 0.860 %,
Temperature -20.0 °C
 1300 ksi

@Strain 0.860 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 251 °C
484 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 232 °C
450 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
 IEC 60695-11-10
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Strength 22.0 kV/mm
559 kV/in
IEC 60243-1
Comparative Tracking Index 125 V
125 V
IEC 60112
200 V
200 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Part Marking Code >PET-GF20FR<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
UL recognition UL
Users viewing this material also viewed the following: