DuPont Performance Polymers Delrin® 500CL BK601 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500CL BK601 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 500CL BK601 is a medium viscosity acetal homopolymer containing a chemical lubricant, designed for low wear and friction against metals.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 67.0 MPa

@Temperature 23.0 °C
9720 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 18 %

@Temperature 23.0 °C
18 %

@Temperature 73.4 °F
nominal; ISO 527
23 %

@Temperature 23.0 °C
23 %

@Temperature 73.4 °F
50mm/min; ISO 527
Elongation at Yield 13 %

@Temperature 23.0 °C
13 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 3.20 GPa

@Temperature 23.0 °C
464 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 2.90 GPa

@Temperature 23.0 °C
421 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO 75-1/-2
UL RTI, Electrical 50.0 °C

@Thickness 0.750 mm
122 °F

@Thickness 0.0295 in
UL 746B
100 °C

@Thickness 1.50 mm
212 °F

@Thickness 0.0591 in
UL 746B
100 °C

@Thickness 3.00 mm
212 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical with Impact 50.0 °C

@Thickness 0.750 mm
122 °F

@Thickness 0.0295 in
UL 746B
80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
UL 746B
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact 50.0 °C

@Thickness 0.750 mm
122 °F

@Thickness 0.0295 in
UL 746B
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
UL 746B
85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL94
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V

@Temperature 23.0 °C
600 V

@Temperature 73.4 °F
IEC 60112
600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
600 V

@Thickness 0.118 in,
Temperature 73.4 °F
UL 746A
Processing Properties Metric English Comments
Melt Temperature 215 °C
419 °F
Optimum; Injection Molding
210 - 220 °C
410 - 428 °F
Injection Molding
Mold Temperature 90.0 °C
194 °F
optimum; Injection Molding
80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.20 %
<= 0.20 %
Injection Molding
Descriptive Properties Value Comments
Additive Lubricant
Appearance Black Color
Drying Recommended Not normally required unless moisture content of resin exceeds recommended level
Features Creep Resistance, Good
Friction, Low
Homopolymer
Lubricated
Stiffness, High
Strength, High
Viscosity, Medium
Wear Resistance, Good
Forms Pellets
Generic Acetal (POM) Homopolymer
Material Status Current
Part Marking Code >POM<
ISO 11469
Polymer Family POM
Polymer Type POM Homopolymer
Processing Method Extrusion
Injection Molding
Product Category Low Wear and Friction Resins
Unreinforced Resins
Region Available - Global Yes
Resin Identification POM
ISO 1043
RoHS Compliance Contact Manufacturer
Ultrasonic Weldable Yes
Uses Automotive Applications
Gears
Parts, Engineering