Dow AFFINITY™ PL 1880G Polyolefin Plastomer (POP)

Category	Polymer , Film , Thermoplastic , Polyolefin
Manufacturer	Dow Chemical
Trade Name	AFFINITY™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow AFFINITY™ PL 1880G Polyolefin Plastomer (POP).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AFFINITY™ PL 1880G is an ethylene alpha-olefin resin produced via INSITE™ Technologies. It is designed for use in a variety of packaging applications, including high-speed, form-fill-seal packaging.Information provided by Dow

Physical Properties	Metric	English	Comments
Density	0.902 g/cc	0.0326 lb/in³	ASTM D792
Thickness	50.8 microns	2.00 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	7.24 MPa	1050 psi	ASTM D882
Film Tensile Strength at Yield, TD	6.89 MPa	1000 psi	ASTM D882
Film Elongation at Break, MD	620 %	620 %	ASTM D882
Film Elongation at Break, TD	630 %	630 %	ASTM D882
Secant Modulus, MD	0.0917 GPa	13.3 ksi	2% Secant; ASTM D882
Secant Modulus, TD	0.0924 GPa	13.4 ksi	2% Secant; ASTM D882
Impact	20.8	20.8	[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
	270	270	[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Puncture Energy	8.81 J	6.50 ft-lb	Dow Method
Elmendorf Tear Strength MD	550 g	550 g	Modified rectangular test specimen; ASTM D1922
Elmendorf Tear Strength TD	720 g	720 g	Modified rectangular test specimen; ASTM D1922
Elmendorf Tear Strength, MD	10.8 g/micron	275 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	14.2 g/micron	360 g/mil	ASTM D1922
Dart Drop Test	>= 830 g	>= 1.83 lb	Method B; ASTM D1709
Film Tensile Strength at Break, MD	58.6 MPa	8500 psi	ASTM D882
Film Tensile Strength at Break, TD	44.7 MPa	6480 psi	ASTM D882
Heat Seal Strength Initiation Temperature	85.0 °C	185 °F	2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method

Thermal Properties	Metric	English	Comments
Melting Point	99.0 °C	210 °F	Dow Method (DSC)
Vicat Softening Point	86.0 °C	187 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	1.1 %	1.1 %	ASTM D1003
Gloss	141 %	141 %	20°; ASTM D2457
Transmission, Visible	83 %	83 %	Clarity; ASTM D1746