DSM Akulon® F223-D (Dry) Low/Medium Viscosity Nylon 6 (North America)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® F223-D (Dry) Low/Medium Viscosity Nylon 6 (North America).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt viscosities to suit all extrusion processes: barrier and coating film, tube and hose, monofilament, stock shapes. Akulon resins are characterized by:consistent qualityhigh purity for film applications, low gel contents. Molding ResinsSuited to all engineering demands: Unfilled low and medium viscosity gradesToughened unfilled gradesGlass reinforced from 20-45% filledLow warpage reinforced gradesFlame retardant; UL V0 rated and glow wire typesHalogen free FR gradesBlow moldable materialsLaser markable resinsLaser weldable, high burst pressure gradesToughened, reinforced resinsHigh stiffness grades for metal replacement Akulon Ultraflow resins have high flow with mechanical properties similar to standard materials. Exceptional flow allows: productivity gains in moldinglower built in stressesbetter surface appearancesystem cost reductions Applications for Molding resins There is an Akulon resin available suitable for any application requiring polyamides. Key areas where DSM has specific application knowledge areAutomotiveUnder the hood and engine componentsExterior and interior applicationsElectrical components and connectorsElectricalLow voltage power distributionLightingPower connectorsConsumer DurablesPower and lawn and garden toolsSmall AppliancesSports and leisure equipmentFurniture accessoriesIndustrial GoodsTransportation (railways)Information provided by DSM.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 10 %
10 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 2.8 %
2.8 %
Humidity Absorption; Sim. to ISO 62
Viscosity Test 129 cm³/g
129 cm³/g
Viscosity Number
Linear Mold Shrinkage, Flow 0.011 cm/cm
0.011 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 85.0 MPa
12300 psi
ISO 527-1/-2
Elongation at Break 20 %
20 %
ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 3.20 GPa
464 ksi
ISO 527-1/-2
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
IEC 60695-11-10
V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
IEC 60695-11-10
Oxygen Index 26 %
26 %
ISO 4589-1/-2
Glow Wire Test 775 °C

@Thickness 38.1 mm
1430 °F

@Thickness 1.50 in
GWIT; IEC 60695-13
800 °C

@Thickness 38.1 mm
1470 °F

@Thickness 1.50 in
GWFI; IEC 60695-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.1

@Frequency 1e+6 Hz
3.1

@Frequency 1e+6 Hz
IEC 60250
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
Dissipation Factor 0.0065

@Frequency 100 Hz
0.0065

@Frequency 100 Hz
IEC 60250
0.0165

@Frequency 1e+6 Hz
0.0165

@Frequency 1e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Injection molding Yes
Release Agent Yes
Without Fillers Yes