Material Notes:
Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or legislations for other countries will be provided on request.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
dry; ISO 1183
Water Absorption 10.5 %
10.5 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 3.2 %
3.2 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 3.3 cP
3.3 cP
ISO Test; 96 % SAV
Viscosity Test 195 cm³/g
195 cm³/g
Viscosity number
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 20 %
20 %
50mm/min; ISO 527
Tensile Modulus 1.00 GPa
145 ksi
1mm/min; ISO 527
Thermal Properties Metric English Comments
Melting Point 196 °C
385 °F
10 K/min
196 °C
385 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
FDA 21 CFR 177.1500 (restrictions per 21 CFR .1395)
Form Pellets
Impact Modified No
Primary Processing Technique Film Extrusion
Processing Other Extrusion