Polymer Property : Melting Point = 196 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Melting Point	196 °C	385 °F	ISO METHOD 3146C
NYCOA 2046 Copolymer Nylon 6/69 extrusion, moderate melt viscosity, high strength mono.Information provided by NYCOA, Inc.
Melting Point	196 - 200 °C	385 - 392 °F	Average value: 197 °C Grade Count:5
Overview of materials for Nylon 6/69 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6/69". Each property range of values reported is minimum and maximum values of appropriate MatWeb ..
Melting Point	196 - 204 Â°C	385 - 400 Â°F	MQSA 111
Lubrizol Advanced Materials PEARLTHANEÂ® Clear 15N80 Thermoplastic Polyurethane Elastomer PEARLTHANEÂ® CLEAR 15N80 is a polyether copolymer-based TPU, supplied in form of translucent, colorless, combining low hardness with excellent mechanical properties and excellent hydrolysis resist..
Melting Point	196 °C	385 °F	ISO 3146
Chengdu Polyster H605B Thermoplastic Polyether-ester Elastomer (TPEE) Medium modulus molding and extrusion grade. Contains color-stable antioxidants. Good balance of low and high temperature properties. Good melt stability. CVJ boots, dust cover, bellows, jackets and ..
Melting Point	196 °C	385 °F	Freezing Point; ASTM D3418
DuPont™ Bynel® 41E766 Anhydride Modified LLDPE BYNEL® Series 4100 series resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All BYNEL Series 4100 series resins are available in pellet form for use in conventional ext..
Melting Point	196 °C	385 °F	ASTM D3418
DuPont Performance Polymers Hytrel® HTR8136BK TPC-ET (Unverified Data**) Hytrel® HTR8136BK is designed for blow molding or processing by techniques requiring high melt viscosity. It has nominal durometer hardness of 49D, is pigmented black with fine particle size carbon..
Melting Point	196 °C	385 °F	ASTM D3418
Ashley Polymers Ashlene® 745 Nylon 6/69 A special copolymer ideal for blown and cast film coextrusion. This is a gel free resin with outstanding lot to lot consistency being produced by a continuous process. It has a lower melting point..
Melting Point	196 °C	385 °F	10 K/min
BASF Ultramid® C33 01 PA66/6 (Conditioned) Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to F..
Melting Point	196 °C	385 °F	ASTM Test
BASF Ultramid® C33 01 PA66/6 (Conditioned) Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to F..
Melting Point	196 °C	385 °F	10 K/min
BASF Ultramid® C33L 01 PA66/6 (Dry) Ultramid C33L 01 is an intermediate viscosity, copolymer 6/66.Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to..
Melting Point	196 °C	385 °F	ASTM D3418
Ashley Polymers Ashlene® 746 Nylon 6/69 A special copolymer ideal for blown and cast film coextrusion. This is a gel free resin with outstanding lot to lot consistency being produced by a continuous process. It has a lower melting point..
Melting Point	196 °C	385 °F	ASTM D3418
Ashley Polymers Ashlene® 747 Nylon 6/66 A medium viscosity copolymer. Excellent flexibility and elongation suitable for film and monofilament applications.Data provided by the manufacturer
Melting Point	196 °C	385 °F	10 K/min
BASF Ultramid® C33 01 PA66/6 (Dry) Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to F..
Melting Point	196 °C	385 °F	ASTM Test
BASF Ultramid® C33 01 PA66/6 (Dry) Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to F..