BASF Ultramid® B3EG3 BK00564 15% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3EG3 BK00564 15% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B3EG3 BK00564 is a 15% glass fiber reinforced, pigmented black injection molding PA6 grade for housings with enhanced impact resistance.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 2.6 %
2.6 %
24 hour; ISO Test
8.0 %
8.0 %
ISO 62
Moisture Absorption at Equilibrium 2.6 %
2.6 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 115 MPa
16700 psi
5mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5mm/min; ISO 527
Tensile Modulus 6.06 GPa
879 ksi
1mm/min; ISO 527
Flexural Modulus 5.30 GPa
769 ksi
ISO Data
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO Test
4.50 kJ/m²

@Temperature -40.0 °C
 2.14 ft-lb/in²

@Temperature -40.0 °F
 ISO Test
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
Descriptive Properties Value Comments
Color BK00564
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding