BASF Capron® 8200 NL Nylon 6 (DAM) (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Capron® 8200 NL Nylon 6 (DAM) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	1.6 %	1.6 %	24 hr.; ISO 62
	9.5 %	9.5 %	ISO 62
Moisture Absorption at Equilibrium	2.7 %	2.7 %	23°C/50% R.H.; ISO 62
Viscosity Measurement	64	64	Formic Acid; ASTM D789
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	MD; ASTM Test

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM D785
Tensile Strength at Break	75.0 MPa	10900 psi	0.2 in/min; ASTM D638
Tensile Strength, Yield	79.0 MPa	11500 psi	50 mm/min; ISO 527
	79.0 MPa	11500 psi	2 in/min; ASTM D638
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM D638
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO 527
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ASTM D638
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ISO 527
	125 MPa @Temperature -40.0 °C	18100 psi @Temperature -40.0 °F	ASTM D638
	125 MPa @Temperature -40.0 °C	18100 psi @Temperature -40.0 °F	ISO 527
Elongation at Break	>= 50 %	>= 50 %	50 mm/min; Nominal; ISO 527
	55 %	55 %	2 in/min; ASTM D638
Elongation at Yield	4.0 %	4.0 %	50 mm/min; ISO 527
	4.0 %	4.0 %	2 in/min; ASTM D638
Modulus of Elasticity	0.360 GPa @Temperature 120 °C	52.2 ksi @Temperature 248 °F	ISO 527
	0.485 GPa @Temperature 80.0 °C	70.3 ksi @Temperature 176 °F	ISO 527
Tensile Modulus	3.10 GPa	450 ksi	1 mm/min; ISO 527
Flexural Strength	110 MPa	16000 psi	ASTM D790
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ASTM D790
	20.0 MPa @Temperature 93.0 °C	2900 psi @Temperature 199 °F	ASTM D790
	30.0 MPa @Temperature 65.0 °C	4350 psi @Temperature 149 °F	ASTM D790
	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ASTM D790
Flexural Modulus	2.83 GPa	410 ksi	ASTM D790
	0.305 GPa @Temperature 120 °C	44.2 ksi @Temperature 248 °F	ASTM D790
	0.350 GPa @Temperature 93.0 °C	50.8 ksi @Temperature 199 °F	ASTM D790
	0.500 GPa @Temperature 65.0 °C	72.5 ksi @Temperature 149 °F	ASTM D790
	3.01 GPa @Temperature -40.0 °C	437 ksi @Temperature -40.0 °F	ASTM D790
Izod Impact, Notched	0.600 J/cm	1.12 ft-lb/in	ASTM D256
	0.500 J/cm @Temperature -40.0 °C	0.937 ft-lb/in @Temperature -40.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	83.0 µm/m-°C @Temperature 20.0 °C	46.1 µin/in-°F @Temperature 68.0 °F	ASTM E831
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	178 °C	352 °F	ISO 75
	178 °C	352 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ISO 75
	65.0 °C	149 °F	ASTM D648

Descriptive Properties	Value	Comments
Additive	Unfilled
Color	Natural
Commercial Status (March 2007)	Active America
Form	Pellets
Impact Modified	No
Injection molding	Processable
Primary Processing Technique	Film Extrusion