Polymer Property : Flexural Strength = 110 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	110 MPa	16000 psi	ISO 178
Nilit FRIANYL B63 H-KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	<= 110 MPa	<= 16000 psi	ISO 178
Polykemi AB SCANAMID 66 A13^ Q2 EX8 Nylon 66, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	110 MPa	16000 psi	ISO 178
Radici Radiflam® AFR (dry) Nylon 66 PA66 Self-extinguishing without halogens or phosphorousInformation provided by Radici group.
Flexural Strength	110 MPa	16000 psi	ASTM D790
Polymer Resources PC/ABS-G10 General Purpose PC/ABS Alloy, 10% Glass Filled PC/ABS Alloy, General Purpose, 10% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi..
Flexural Strength	110 MPa	16000 psi	ASTM D790
Ravago Manufacturing Americas Hylon® N2000HL Nylon 6 (DAM) Information provided by Ravago.
Flexural Strength	110 MPa	16000 psi	ASTM D790
PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6) Information provided by PolyOne
Flexural Strength	110 MPa	16000 psi	ASTM D790
PolyOne Edgetek® PS-25MN/000 Polybutylene Terephthalate (PBT), Mineral Filled (discontinued **) Description/Features:Mineral FilledUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
Flexural Strength	110 MPa	16000 psi	1.3 mm/min; ASTM D790
PolyOne Edgetek® AS-30GF/000 BLACK Acrylonitrile Butadiene Styrene (ABS) Information provided by PolyOne
Flexural Strength	110 MPa	16000 psi
Lehmann & Voss LUVOCOMÂ® 19-8043 Polyamide 46, with PTFE, lubricant modified, high viscosity Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..
Flexural Strength	110 MPa @Temperature 149 Â°C	16000 psi @Temperature 300 Â°F
Greene Tweed ArlonÂ® 2000 Polyketone ArlonÂ® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie..
Flexural Strength	110 MPa	16000 psi
Lehmann & Voss LUVOCOMÂ® 1-7139-1 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Improved heat resistance.Control disks, cams, sliding elements and o..
Flexural Strength	110 MPa	16000 psi	ISO 178
Solvay TECHNYLÂ® B 52 G1 MX 35 (XA 3004) PA66/6 Description: TECHNYL B 52 G1 MX35 is a copolyamide 6.6/6 , with thermal protection, glow wire resistant and reinforced with mineral filler.Colors: GreyAvailable in: Latin AmericaMain Properties: ? G..
Flexural Strength	110 MPa	16000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm.
Flexural Strength	110 MPa	16000 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 226 Nylon 6.6 SAXAMID 226 is a general purpose polyamide 6.6 injection-molding-grade. Benefits are short cycle times and good release properties.Information provided by SAX Polymers
Flexural Strength	110 MPa	16000 psi	ASTM D790
A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman.
Flexural Strength	110 - 130 MPa	16000 - 18900 psi	At Rupture; ISO 178
Vyncolit 4221 XB Novolac Phenolic Mineral and organic filled phenolic molding compound with good mechanical properties.Information provided by Vyncolit, a Sumitomo Bak Group
Flexural Strength	110 MPa	16000 psi	ISO 178
Polyram PlusTek PA801 Nylon 6.6 Copolymer for Injection Molding, Impact Modified Impact modified Nylon 6.6 copolymer for injection molding application.Information provided by Polyram.
Flexural Strength	110 MPa	16000 psi	ASTM D790
Polyram PlusTek PB702 Nylon 6, UV Stabilized Polyamide 6 UV stabilized for fast cycle injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	110 MPa	16000 psi	ISO 178-93
Wellman Wellamid® GF10-66/6-LI6-NBK4 10% Glass Reinforced, Toughened Nylon 66/6 Description: Glass Reinforced, Toughened Nylon 66/6Information provided by Wellman.
Flexural Strength	110 MPa	16000 psi	ASTM D790
Polyram PlusTek PB901 Nylon 6, Extruded cable coating Polyamide 6 for very thin electrical extruded cable coatingInformation provided by Polyram Ram On Ind.
Flexural Strength	110 MPa	16000 psi	ISO 178
Polyram RamShine PV3003R2 Acrylonitrile Butadiene Styrene, 10% Carbon Fiber 10% Carbon fiber reinforced ABS for injection molding applications.Information provided by Polyram.
Flexural Strength	110 MPa	16000 psi	ISO 178
Eurostar Starflam PK0052E PA6, 25% Mineral Filled, Injection Molded PK0052E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Mineral Filed, Polyamide 6 Injection Molding (also known as PM3520Z222 or PA 25E6 U9 Z22)Information provided by Polymer Technolo..
Flexural Strength	<= 110 MPa	<= 16000 psi	3.5% flexure; ISO 178
Azoty Tarnow™ Tarnamid® T-27 MK30 Polyamide 6 - Mineral Reinforced 30% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechani..
Flexural Strength	110 MPa	16000 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 247 SAN, Glass/Mineral Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	110 - 138 MPa	16000 - 20000 psi
Bulk Molding Compounds BMC 5436 Mineral Filled, Glass Reinforced Polyester BMC 5436 molding compound is a low cost, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is characterized by good molda..
Flexural Strength	110 - 138 MPa	16000 - 20000 psi
Bulk Molding Compounds BMC 2274 Mineral Filled, Glass Reinforced Polyester BMC 2274 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression transfer and stuffer injection molding. It is a general-purpose material with medium..
Flexural Strength	110 - 130 MPa	16000 - 18900 psi	Injection; ISO 178
Raschig Group 5557 DAP (discontinued **) Glass fiber-reinforced and inorganically filled diallylphthalate molding compound (DAP) in various colors. Good mechanical strength together with retention of high electrical properties under hot h..