Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 21SPF1 is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding applications with the added benefits of improved flow during the molding process. This resin offers a the same well balanced combination of engineering properties characterized by high strength; rigidity; good toughness, high melt point, good surface lubricity; abrasion resistance and resistance to many chemical, machine and motor oils, solvents and gasoline. Vydyne 21SPF1 permits production of molded parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal and military specifications for premium-quality, general-purpose PA66 resins. Vydyne 21SPF1 resin is internally and externally lubricated for improved machine feed and exceptional mold release. It is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity. Vydyne 21SPF1 can reduce or eliminate the need for mold release sprays. Critical molded-part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis. Typical Applications/End Uses: Vydyne 21 SPF1 has been used in many molding applications such as terminal blocks bearings, bushings, cams, electrical connectors and housings, electrical cable ties/tie straps and many other hardware and general industrial parts.Availability:Asia PacificEuropeNorth AmericaAdditive: Lubricant Features:Fast Molding CycleGasoline ResistanceGood Abrasion ResistanceGood Chemical ResistanceGood Mold ReleaseGood ToughnessHigh RigidityHigh StrengthLubricatedOil ResistantSolvent ResistantUses:BearingsBushingsCamsConnectorsElectrical HousingsIndustrial ApplicationsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
1.2 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Diameter 2.00 mm
0.020 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.020 cm/cm

@Diameter 2.00 mm
0.020 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527-2
Tensile Strength, Yield 88.0 MPa
12800 psi
ISO 527-2
Elongation at Break 20 %
20 %
ISO 527-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-2
Tensile Modulus 3.30 GPa
479 ksi
ISO 527-2
Flexural Strength 105 MPa
15200 psi
ISO 178
Flexural Modulus 3.30 GPa
479 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 180
6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C
162 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
UL 746
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.710 mm
167 °F

@Thickness 0.0280 in
UL 746
75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.710 mm
185 °F

@Thickness 0.0280 in
UL 746
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
UL 746
85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-2

@Thickness 0.710 mm
V-2

@Thickness 0.0280 in
V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Oxygen Index 26 %
26 %
ISO 4589-2
Glow Wire Test 700 °C

@Thickness 0.710 mm
1290 °F

@Thickness 0.0280 in
Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
1290 °F

@Thickness 0.0591 in
Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
1290 °F

@Thickness 0.118 in
Ignition Temperature; IEC 60695-2-13
800 °C

@Thickness 0.710 mm
1470 °F

@Thickness 0.0280 in
Flammability Index; IEC 60695-2-12
800 °C

@Thickness 1.50 mm
1470 °F

@Thickness 0.0591 in
Flammability Index; IEC 60695-2-12
930 °C

@Thickness 3.00 mm
1710 °F

@Thickness 0.118 in
Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 26.0 kV/mm

@Thickness 1.00 mm
660 kV/in

@Thickness 0.0394 in
IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
120 - 179 sec

@Thickness 0.118 in
ASTM D495
Comparative Tracking Index 600 V

@Thickness 3.00 mm
600 V

@Thickness 0.118 in
IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.710 mm
7.0 - 14 sec

@Thickness 0.0280 in
UL 746
15 - 29 sec

@Thickness 1.50 mm
15 - 29 sec

@Thickness 0.0591 in
UL 746
15 - 29 sec

@Thickness 3.00 mm
15 - 29 sec

@Thickness 0.118 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.710 mm
>= 120 arcs

@Thickness 0.0280 in
UL 746
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Middle Barrel Temperature 270 - 285 °C
518 - 545 °F
Front Barrel Temperature 280 - 290 °C
536 - 554 °F
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Melt Temperature 285 - 300 °C
545 - 572 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature <= 70.0 °C
<= 158 °F
Dry Time 1.00 - 3.00 hour
1.00 - 3.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 50 %