Lanxess Pocan® B 4215 000000 PBT, 12% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® B 4215 000000 PBT, 12% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 12% glass fibers, injection molding, flame retardant
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.10 %
0.10 %
23°C/50% R.H.; Test Sim. to ISO 62
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 260 °C
25 g/10 min

@Load 4.76 lb,
Temperature 500 °F
Calculated from MVR using melt density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 5.70 GPa
827 ksi
ISO 527-1/-2
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 5500 MPa
798000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 5000 MPa
725000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 70.0 °C
158 °F
ISO 75-1/-2
Vicat Softening Point 205 °C
401 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
IEC 60695-11-10
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695-11-10
5VA

@Thickness 3.50 mm
5VA

@Thickness 0.138 in
IEC 60695-11-20
Oxygen Index 32 %
32 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 100 Hz
0.0040

@Frequency 100 Hz
IEC 60250
0.019

@Frequency 1.00e+6 Hz
0.019

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 200 V
200 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Features Flame retardant
Form Pellets
ISO Shortname ISO 7792-1-PBT,GFHMR,09-060,GF12; ISO 1043-PBT GF FR(17)
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America