Arkema Group Pebax® 6333 SP 01 Polyether Block Amide (PEBA)

Category Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer Arkema
Trade Name Pebax®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Pebax® 6333 SP 01 Polyether Block Amide (PEBA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether block amide PEBAX® 6333 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SP grade has been developed to be heat and UV resistant.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Water Absorption 1.1 %

@Temperature 23.0 °C,
Time 86400 sec
1.1 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.70 %

@Temperature 20.0 °C
0.70 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.012 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.012 in/in

@Thickness 0.157 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.014 in/in

@Thickness 0.157 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 64
64
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
58

@Time 15.0 sec
58

@Time 0.00417 hour
Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 53.0 MPa
7690 psi
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break >= 350 %
>= 350 %
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus 0.285 GPa
41.3 ksi
Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 169 °C
336 °F
ISO 11357
Vicat Softening Point 157 °C

@Load 1.02 kg
315 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 225 °C
437 °F
Recommended Extrusion Temperature
210 - 240 °C
410 - 464 °F
Extrusion Range
Nozzle Temperature 260 °C
500 °F
Recommended
230 - 290 °C
446 - 554 °F
Mold Temperature 25.0 - 60.0 °C
77.0 - 140 °F
Drying Temperature 65.0 - 75.0 °C
149 - 167 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour