3M Scotch-Weld™ DP8010NS Structural Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ DP8010NS Structural Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010NS is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropylene, Polyethylene, and TPO’s with out special surface preparation. It can replace screws, rivet, plastic welding, and two-step processes which include chemical etchants, priming or surface treatments in many applications. DP-8010NS is a non-sag product designed to be used in applications where a high viscosity product is needed such as a vertical surface.Information provided by 3M

Physical Properties	Metric	English	Comments
Brookfield Viscosity	27000 cP	27000 cP	Acecelerator, DV-II, #7 sp, 20 rpm
	70000 cP	70000 cP	Base, DV-II, #7 sp, 20 rpm

Mechanical Properties	Metric	English	Comments
Shear Strength	0.345 MPa	50.0 psi	Overlap, Toluene for 14 days, Cohesive Failure
	0.862 MPa	125 psi	Overlap, Al/HDPE (non-abraded aluminum), Adhesive Failure to Al
	1.03 MPa	150 psi	Overlap, Acetal, Adhesive Failure
	1.90 MPa	275 psi	Overlap, Acetone for 14 days, Cohesive Failure
	2.76 MPa	400 psi	Overlap, LDPE, Substrate Failure
	3.28 MPa	475 psi	Overlap, PTFE, Adhesive Failure
	3.96 MPa	575 psi	Overlap, HIPS, Substrate Failure
	3.96 MPa	575 psi	Overlap, Gasoline for 14 days, Cohesive Failure
	4.14 MPa	600 psi	Overlap, Glass (3/16" thick), Substrate Failure
	4.14 MPa	600 psi	Overlap, RK8010A Top Coat CRS/HDPE, Adhesive Failure
	5.17 MPa	750 psi	Overlap, Polystyrene, Substrate Failure
	5.34 MPa	775 psi	Overlap, UHMWPE, Substrate Failure
	5.86 MPa	850 psi	Overlap, CRS/HDPE, Adhesive Failure to CRS
	6.03 MPa	875 psi	Overlap, HCl for 14 days, Substrate Failure
	6.03 MPa	875 psi	Overlap, Isopropyl Alcohol for 14 days, Substrate Failure
	6.21 MPa	900 psi	Overlap, 71°C/100% RH for 14 days, AF/CF
	6.38 MPa	925 psi	Overlap, Diesel Fuel for 14 days, Substrate Failure
	6.55 MPa	950 psi	Overlap, PE, Substrate Failure
	6.55 MPa	950 psi	Overlap, DCT 5002X Top Coat CRS/HDPE (non-abraded CRS), AF/Top Coat
	6.55 MPa	950 psi	Overlap, NaOH for 14 days, Substrate Failure
	6.72 MPa	975 psi	Overlap, Antifreeze Coolant for 14 days, Substrate Failure
	7.067 MPa	1025 psi	Overlap, ED-5000 E-Coated CRS/HDPE, Adhesive Failure
	7.24 MPa	1050 psi	Overlap, Lexan, AF/CF
	7.58 MPa	1100 psi	Overlap, HDPE, Substrate Failure
	7.58 MPa	1100 psi	Overlap, Control, Substrate Failure
	7.93 MPa	1150 psi	Overlap, PP, Substrate Failure
	7.93 MPa	1150 psi	Overlap, Plexiglass (PMMA), Substrate Failure
	8.101 MPa	1175 psi	Overlap, 71°C water soak for 14 days, Cohesive Failure
	8.27 MPa	1200 psi	Overlap, 304 Stainless Steel (1/32" thick), Adhesive Failure
	9.480 MPa	1375 psi	Overlap, EC 3924 Primed CRS (non-abraded CRS), AF/CF
	10.0 MPa	1450 psi	Overlap, Gel Coat (3/16" thick), Substrate Failure
	10.17 MPa	1475 psi	Overlap, ABS, Substrate Failure
	10.3 MPa	1500 psi	Overlap, EC 3924 Primed Al/HDPE (non-abraded Al), Cohesive Failure
	12.93 MPa	1875 psi	Overlap, Copper (1/16" thick), AF/CF
	13.4 MPa	1950 psi	Overlap, Aluminum (1/16" thick), Adhesive Failure
	14.1 MPa	2050 psi	Overlap, PVC, Substrate Failure
	14.1 MPa	2050 psi	Overlap, CRS (1/32" thick), Adhesive Failure
	17.41 MPa	2525 psi	Overlap, Green FRP, AF/CF
	2.76 MPa @Temperature 82.0 °C	400 psi @Temperature 180 °F	Overlap
	16.5 MPa @Temperature 24.0 °C	2400 psi @Temperature 75.2 °F	Overlap
Peel Strength	5.26 kN/m	30.0 pli	T-Peel
	5.26 kN/m	30.0 pli	T-Peel, HDPE, Substrate Failure

Thermal Properties	Metric	English	Comments
CTE, linear	132 µm/m-°C	73.3 µin/in-°F	Below Tg
	207 µm/m-°C	115 µin/in-°F	Above Tg
Glass Transition Temp, Tg	34.0 °C	93.2 °F	onset

Processing Properties	Metric	English	Comments
Cure Time	90.0 - 120 min	1.50 - 2.00 hour	Time to Handling Strength
	480 - 1440 min	8.00 - 24.0 hour	Full Cure

Descriptive Properties	Value	Comments
Appearance	Pink/Amber	Base
	White	Accelerator
	Yellow