NOVA Chemicals Novapol® LA-0219-A LDPE Foam Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® LA-0219-A LDPE Foam Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good heat sealing latitudeModerate toughnessEasy processability Applications: Industrial packagingLinersBlends with LLDPEFoam ArticlesInformation provided by Nova Chemicals
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D792
Thickness 38.0 microns
1.50 mil
Melt Flow 2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.96 MPa
1300 psi
ASTM D882
Tensile Strength, Yield 8.80 MPa
1280 psi
ASTM D638
Film Elongation at Yield, MD 350 %
350 %
ASTM D882
Film Elongation at Yield, TD 550 %
550 %
ASTM D882
Elongation at Break 712 %
712 %
ASTM D638
Flexural Modulus 0.296 GPa
42.9 ksi
0.01; ASTM D790
Puncture Energy 1.71 J
1.26 ft-lb
NOVA test
Coefficient of Friction >= 0.60
>= 0.60
ASTM D1894
Elmendorf Tear Strength MD 225 g
225 g
ASTM D1922
Elmendorf Tear Strength TD 150 g
150 g
ASTM D1922
Dart Drop Test 90.0 g
0.198 lb
F<sub>50</sub>; ASTM D1709/A
Film Tensile Strength at Break, MD 17.9 MPa
2600 psi
ASTM D882
Film Tensile Strength at Break, TD 15.9 MPa
2300 psi
ASTM D882
1% Secant Modulus, MD 152 MPa
22000 psi
ASTM D882
1% Secant Modulus, TD 176 MPa
25500 psi
ASTM D882
Optical Properties Metric English Comments
Haze 12 %
12 %
ASTM D1003
Gloss 40 %
40 %
at 45°; ASTM D2457