- Polymer Property : Cure Time = 6.00 hour
Polymer Property : Cure Time = 6.00 hour Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 360 min | 6.00 hour | Ambient Set |
| Reltek BONDiT™ B-482 Adhesive, Sealant & Coating System Key Properties: Excellent balance of chemical, electrical, and mechanical properties.Ruggedized, semi-flexible system.Very clean system.Ease of use.Applications: Encapsule sensitive instrumentation .. |
|||
| Cure Time | 360 min | 6.00 hour | Ambient Set |
| Reltek BONDiT™ B-481 Adhesive, Sealant & Coating System Key Properties: High strength and toughness with excellent thermal stability to 400°F.Outstanding chemical resistance.Excellent electrical, and mechanical properties.Ease of use.Applications: Encap.. |
|||
| Cure Time | 360 - 480 min @Temperature 25.0 °C |
6.00 - 8.00 hour @Temperature 77.0 °F |
Full Cure |
| Fibre Glast 1101 High-Strength General Purpose Epoxy Adhesive Description:#1101 is a light grayish-tan two part epoxy adhesive that was developed especially for difficult bonding problems involving similar or dissimilar materials. #1101 provides excellent adhe.. |
|||
| Cure Time | 360 min @Temperature 25.0 °C |
6.00 hour @Temperature 77.0 °F |
50% relative humidity |
| Lord Adhesives Aeroglaze® K3425 Sandable Primer/Surfacer For application on epoxy graphite or other plastic substrates or over a suitable primer on metal.Limitations - Aeroglaze® K3425 primer/surfacer contains no inhibiting pigments and is not suitable.. |
|||
| Cure Time | 360 min | 6.00 hour | To depth of 3.2 mm |
| Momentive Performance Materials RTV5242 Neutral Cure, One Component RTV Adhesive Sealant RTV5240 series sealants are alkoxy neutral cure, one-component, ready to use, electronic grade silicone adhesive sealants exhibiting high strength that will maintain a strong bond even when exposed .. |
|||
| Cure Time | 360 min | 6.00 hour | To depth of 3.2 mm |
| Momentive Performance Materials RTV5243 Neutral Cure, One Component RTV Adhesive Sealant RTV5240 series sealants are alkoxy neutral cure, one-component, ready to use, electronic grade silicone adhesive sealants exhibiting high strength that will maintain a strong bond even when exposed .. |
|||
| Cure Time | 360 min | 6.00 hour | To depth of 3.2 mm |
| Momentive Performance Materials RTV5249 Neutral Cure, One Component RTV Adhesive Sealant RTV5240 series sealants are alkoxy neutral cure, one-component, ready to use, electronic grade silicone adhesive sealants exhibiting high strength that will maintain a strong bond even when exposed .. |
|||
| Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack-free |
| Sika Industry SikaFlex 219 LM Low Modulus Polyurethane Sealant Sika 219 LM SikaFlex Low Modulus Polyurethane SealantThis is a high performance, low modulus polyurethane base, non-sag elastomeric sealant with excellent adhesion to a wide variety of substrates. M.. |
|||
| Cure Time | 360 min | 6.00 hour | 2 hrs @ 65°C + 4 hrs @ 130°C |
| Tra-Con Tra-Bond 2208 Water White High Temperature Epoxy Adhesive TRA-BOND 2208 is a clear, almost water-white low viscosity epoxy adhesive system recommended for rigid laminating, filament winding, potting and bonding applications. This all-liquid formulation con.. |
|||
| Cure Time | 360 min | 6.00 hour | 4 hrs @ 25°C + 2 hrs @ 65°C |
| Tra-Con Tra-Cast 3101 Encapsulating Adhesive System TRA-CAST 3101 is an easy-to-use, room temperature cure, rigid, low viscosity, 100% solids (no solvents) epoxy resin and hardener system with excellent mechanical and electrical properties. It is rec.. |
|||
| Cure Time | 360 min | 6.00 hour | 4 hrs @ 25°C + 2 hrs @ 65°C |
| Tra-Con Tra-Cast 3104 Low Viscosity Epoxy Casting Compound TRA-CAST 3104 is a low viscosity, room temperature cure epoxy casting system developed for high performance production encapsulation and impregnating applications where filling fine intricate free s.. |
|||
| Cure Time | 360 min | 6.00 hour | 4 hrs @ 25°C + 2 hrs @ 65°C |
| Tra-Con Tra-Cast 3110 Low Density Epoxy Casting System TRA-CAST 3110 is a unicellular, low density, syntactic-foam epoxy resin casting system of medium viscosity that easily handles, mixes and cures at room temperature. Developed for industrial encapsul.. |
|||
| Cure Time | 360 min | 6.00 hour | 4 hrs @ 25°C + 2 hrs @ 65°C |
| Tra-Con Tra-Cast 3107 Low Shrinkage Epoxy Casting System TRA-CAST 3107 is a versatile epoxy casting system developed for high performance production potting, encapsulating, casting and tooling applications where low shrinkage, easy handling and flowabilit.. |
|||
| Cure Time | 360 min | 6.00 hour | 4 hrs @ 25°C + 2 hrs @ 65°C |
| Tra-Con Tra-Cast 3143 Fire Retardant Epoxy Casting Compound TRA-CAST 3143 has a low viscosity and long pot life. It is certified to the requirements of UL 94 V-O, and is recommended for rigid potting, laminating, transformer encapsulating, filament winding a.. |
|||
| Cure Time | 360 - 2880 min | 6.00 - 48.0 hour | Full Cure; Unprimed |
| Loctite® Gasket Eliminator® 509 Flange Sealant Anaerobic GasketingLoctite® 509 Flexible Cure Gasket Eliminator® Flange SealantProduct withstands minor flange movements caused by vibrations. It will not run when applied to vertical surfaces. F.. |
|||
| Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
| ACC QM 107 QSI Quantum Silicones 7 Durometer Condensation Cure Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is us.. |
|||
| Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
| ACC QM 122 QSI Quantum Silicones 22 Durometer Condensation Cured Moldmaking Material QM 122 is a two-component, room temperature condensation cure silicone material. The cured rubber is flexible with excellent mechanical and physical properties in addition to good shelf-life stabili.. |
|||
| Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
| ACC QM128 QSI Quantum Silicones 28 Durometer Condensation Cured Moldmaking Material QM 128 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and shelf-life stability. This material is an excellent choice f.. |
|||
| Cure Time | 360 min | 6.00 hour | Touch Dry |
| 3M Scotchkote™ CR 511 Epoxy Ceramic Surface Scotchkote Epoxy Ceramic CR 511 has been specifically developed as a 100% solids coating for resurfacing and lining to improve the efficiency of equipment in fluid flow environments.Product Features.. |
|||
| Cure Time | 360 min | 6.00 hour | Hard Dry, 1 hr when surface temp at 50°C |
| 3M Scotchkote™ 162PWX Epoxy Coating 3M Scotchkote Epoxy Coating 162PWX is a 100% solid two-part epoxy coating that has been specifically developed for the long term protection of drinking water pipelines, storage and process tanks or .. |
|||
| Cure Time | 360 min | 6.00 hour | Hard Dry |
| 3M Scotchkote™ 165HB Urethane Coating 3M Scotchkote Urethane Coating 165HB is a two component 100% solids urethane coating used for the internal and external protection of steel and concrete pipes, tanks, and vessels. It can be used in .. |
|||
| Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Time to Handling Strength |
| 3M Scotch-Weld™ DP640 Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-part, non-sag urethane adhesives. They feature tough, flexible bonds with good adhesion to a wide variety of substrates especially wood and many properl.. |
|||
| Cure Time | 360 min | 6.00 hour | |
| 3M AC-730 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
| Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
| ACC QM 113 QSI Quantum Silicones 13 Durometer Condensation Cured Moldmaking Material QM 113 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is an.. |
|||
| Cure Time | 360 - 2880 min | 6.00 - 48.0 hour | Full Cure; Unprimed |
| Loctite® 573 Semi-rigid Cure Anaerobic Sealant Anaerobic GasketingLoctite® 573 Semi-rigid Cure Anaerobic SealantRecommended Primer: 7649 (N). Typical Use: Slow curing for extended assembly operations |
|||