Polymer Property : Cure Time = 7.00 hour Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	360 - 420 min	6.00 - 7.00 hour	Tack-Free Time
3M AC-350 Class C-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav..
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 575-N High Temperature Potting & Casting Material Alumina Fine grain castable for potting and producing small tools.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 576-N High Temperature Potting & Casting Alumina Medium grain castable ceramic for large high temperature potting and tooling. Aremco offers a range of ceramic-based materials used for the assembly of high temperature, high power electrical devic..
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 586 High Temperature Potting & Casting Material Zirconia Silicate Castable ceramic for ceramic and metal assemblies. Excellent handling, fast curing.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 645-N High Temperature Potting & Casting Material Silica Castable ceramic with low thermal conductivity.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 646-N High Temperature Potting & Casting Material Zirconia Castable ceramic with high dielectric and physical strength.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 673-N High Temperature Potting & Casting Material Silicon Carbide Single-part castable ceramic exhibiting high strength and thermal conductivity.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 675 High Temperature Potting & Casting Material Aluminum Nitride Fine grain aluminum nitride castable with high thermal conductivity
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 675-N High Temperature Potting & Casting Material Aluminum Nitride Fine grain aluminum nitride castable with high thermal conductivity.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 895 High Temperature Potting & Casting Material Alumina Fine grain castable ceramic.
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs at 200°F; 3 hrs at 250°F
Aremco Ceramacast™ 900 High Temperature Potting & Casting Material Zirconia Silicate High Density, high strength molding compound.
Cure Time	360 - 420 min	6.00 - 7.00 hour	Tack-Free Time
3M AC-370 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven..
Cure Time	360 - 420 min	6.00 - 7.00 hour
3M AC-370 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven..
Cure Time	300 - 420 min	5.00 - 7.00 hour	2-4 hrs Air Set; 3 hrs at 200°F
Aremco Pyro-Putty™ 2500 High Temperature Ceramic-Metallic Putty, Iron Oxide Filled Ceramic and Black Iron Oxide-Filled, One-Part, Water Based Paste.For Applications to 1/4" Thick.Repairs Cast Iron, and Steel Parts to 1600°F