Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 360 - 480 min @Temperature 23.0 °C |
6.00 - 8.00 hour @Temperature 73.4 °F |
|
Resin Technology Group 6850FTLVDP Oxy-Bond™ Two component Potting Compound Resin Technology Group 6850FTLVDP Oxy-Cast™ Two component Potting CompoundLow viscosity, 2:1 ratio, Potting compound with high thermal conductivity |
|||
Cure Time | 1.00 - 480 min @Temperature 71.1 - 204 °C |
0.0167 - 8.00 hour @Temperature 160 - 400 °F |
Average value: 71.3 min Grade Count:32 |
Overview of materials for Epoxy, High Temperature This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Mineral Filled". Each property range of values reported is minimum and maximum val.. |
|||
Cure Time | 360 - 480 min @Temperature 25.0 °C |
6.00 - 8.00 hour @Temperature 77.0 °F |
Full Cure |
Fibre Glast 1101 High-Strength General Purpose Epoxy Adhesive Description:#1101 is a light grayish-tan two part epoxy adhesive that was developed especially for difficult bonding problems involving similar or dissimilar materials. #1101 provides excellent adhe.. |
|||
Cure Time | 240 - 480 min | 4.00 - 8.00 hour | Tack-free |
Sika Industry SikaFlex 201 Adhesive Sika 201 SikaFlex AdhesiveSikaflex 201 meets Federal Specification TT-S-00230C, Type II, Class A and ASTK C-920, Type S, Grade NS. 15 - 15 mm Cut-Off. Good non-sag. Available in black, white, gray, .. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack-free |
Sika Industry SikaFlex 219 LM Low Modulus Polyurethane Sealant Sika 219 LM SikaFlex Low Modulus Polyurethane SealantThis is a high performance, low modulus polyurethane base, non-sag elastomeric sealant with excellent adhesion to a wide variety of substrates. M.. |
|||
Cure Time | 240 - 480 min @Temperature 177 °C |
4.00 - 8.00 hour @Temperature 350 °F |
|
Master Bond EP36CLV One Component Heat Resistant Liquid Flexible Epoxy Master Bond Polymer System EP36CLV is a one component, high temperature resistant, B staged epoxy that cures with excellent toughness and is far less rigid than typical high temperature resistant ep.. |
|||
Cure Time | 240 - 480 min @Temperature 23.0 °C |
4.00 - 8.00 hour @Temperature 73.4 °F |
|
Master Bond EP77M-F Silver Conductive, Fast Curing Epoxy Adhesive Master Bond Polymer System EP77M-F is a two component, silver filled, electrically conductive adhesive for high performance bonding formulated to cure very rapidly at room temperature. Unlike the ma.. |
|||
Cure Time | 420 - 480 min | 7.00 - 8.00 hour | Tack-Free Time |
3M AC-350 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Cure Time | 420 - 480 min | 7.00 - 8.00 hour | |
3M AC-350 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are.. |
|||
Cure Time | 420 - 480 min | 7.00 - 8.00 hour | Tack-Free Time |
3M AC-770 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-770 Class B are fast cure, low density two-component, manganese dioxide cure, polysulfide fuselage sealants. 3M AC-770 Class B Sealants have outstanding resistance to aviatio.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
ACC QM 107 QSI Quantum Silicones 7 Durometer Condensation Cure Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is us.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
ACC QM 118 QSI Quantum Silicones 18 Durometer Condensation Cured Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is an.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
ACC QM 122 QSI Quantum Silicones 22 Durometer Condensation Cured Moldmaking Material QM 122 is a two-component, room temperature condensation cure silicone material. The cured rubber is flexible with excellent mechanical and physical properties in addition to good shelf-life stabili.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
ACC QM128 QSI Quantum Silicones 28 Durometer Condensation Cured Moldmaking Material QM 128 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and shelf-life stability. This material is an excellent choice f.. |
|||
Cure Time | 360 - 480 min @Temperature 24.0 °C |
6.00 - 8.00 hour @Temperature 75.2 °F |
|
BCC Products BC 5003 Epoxy Laminating System BC 5003 is a medium viscosity, unfilled laminating system. It is a room temperature curing resin with a relatively short pot life. BC 5003 is also considered an excellent general purpose adhesive fo.. |
|||
Cure Time | 420 - 480 min | 7.00 - 8.00 hour | Tack-Free Time |
3M AC-370 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Time to Handling Strength |
3M Scotch-Weld™ DP640 Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-part, non-sag urethane adhesives. They feature tough, flexible bonds with good adhesion to a wide variety of substrates especially wood and many properl.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | demold time |
BCC Products BC 8860 Polyurethane Elastomer BC8860 is a low viscosity two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use for the production casting of hig.. |
|||
Cure Time | 360 - 480 min | 6.00 - 8.00 hour | Tack Free Time, catalyzed with QM cat BLUE |
ACC QM 113 QSI Quantum Silicones 13 Durometer Condensation Cured Moldmaking Material QM 113 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is an.. |
|||
Cure Time | 240 - 480 min | 4.00 - 8.00 hour | Mixture reaches handling strength in 4 to 8 hours. |
Fibre Glast 88 / 87 General Purpose Epoxy Resin and Hardener
(discontinued **) Description:#88 Epoxy Resin is a 100% reactive low viscosity liquid bisphenol-A based epoxy resin diluted with Alkyl glycidyl ether. This resin is specially designed for applications requiring low v.. |