Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | |
3M Dyneon™ Fluorel™ FE-5623Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | |
3M Dyneon™ Fluorel™ FC-2174 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent processability. Suggested .. |
|||
Tensile Strength, Ultimate | 17.0 - 32.4 MPa | 2470 - 4700 psi | Average value: 25.1 MPa Grade Count:10 |
Overview of materials for Thermoplastic Olefinic Elastomer (TPO), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Olefinic Elastomer (TPO), Blow Molding Grade". Each property range of values reported is m.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-701 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt, 10.5% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughnes.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-705 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt index, 13.3% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and t.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-760 High EVA Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 27.5% vinyl acetate copolymer designed for specialty compounding applications. Excellent filler acceptance produces highly loaded concentrates.Ap.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-613 EVA Injection Molding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 8.8% vinyl acetate copolymer resin designed for molding and extrusion applications requiring low temperatures, flexibility and toughness. This r.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Huntsman PE1504 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 55BZ+5Mos PTFE; Bronze/Molybdenum Disulphide Filled
(discontinued **) Data provided by the manufacturer.55 wt.% Bronze + 5 wt.% MoS2. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric properti.. |
|||
Tensile Strength, Ultimate | 17.0 - 827 MPa | 2470 - 120000 psi | Average value: 79.8 MPa Grade Count:368 |
Overview of materials for Nylon 12 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12". Each property range of values reported is minimum and maximum values of appropriate MatWeb en.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Compounded Tire |
Polybutadiene Rubber (BR) |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Compounded Tire |
Butyl Rubber (IIR, CIIR, BIIR) Butyl rubber is a copolymer of isoprene (minor) and isobutylene. Chlorobutyl (CIIR) and Bromobutyl (BIIR) contains 1.2% of the halogen. The halogen addition changes the cure characteristics and ca.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D412 |
KKPC KOSYN KTR 301 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics .. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ CA187 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus, paintable thermoplastic elastomeric olefin resin, excellent paintability, excellent surface appearance, good impact and stiffness balanceApplications:.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ CB229 Thermoplastic Olefin Resin Key Features: medium high melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, excellent processabili.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 395 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 265 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 395 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 341 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 341 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638/D412 |
Covestro Baydur® SFR-243 Polyurethane Composite RRIM Foam, 15% Milled Glass Filled, MDI-based 2-Component Liquid System 0.25 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – C.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638/D412 |
Covestro Bayflex® XGT-16 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 152 Polypropylene, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 17.0 MPa @Temperature 250 °C |
2470 psi @Temperature 482 °F |
ASTM D638 |
Asahi Glass Fluon® P-802UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 35CAR PTFE; Petroleum Coke and Graphite
(discontinued **) Data provided by the manufacturer.35 wt.% Petroleum Coke and Graphite. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric p.. |
|||
Tensile Strength, Ultimate | 17.0 - 148 MPa | 2470 - 21500 psi | Average value: 70.8 MPa Grade Count:72 |
Overview of materials for Nylon 6, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum v.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-712 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt, 10% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughness... |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
LyondellBasell Astryn 73A6-3 Polypropylene Copolymer, 30% Calcium Carbonate Key Features: medium high melt flow, medium modulus, mineral-filled polypropylene copolymer, excellent impact and stiffness balance, excellent chemical resistance, excellent aesthetics, high gloss, .. |
|||
Tensile Strength, Ultimate | 17.0 - 303 MPa | 2470 - 43900 psi | Average value: 115 MPa Grade Count:6 |
Overview of materials for Thermoset Polyurethane Foam, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane Foam, Glass Filled". Each property range of values reported is minimum and maximu.. |