ExxonMobil Escorene® LD-613 EVA Injection Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate; Molded/Extruded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD-613 EVA Injection Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.An 8.8% vinyl acetate copolymer resin designed for molding and extrusion applications requiring low temperatures, flexibility and toughness. This resin can also be considered for blending with homopolymer resins to improve their toughness.Applications: Large injection molded shapes.

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	Exxon Method
Environmental Stress Crack Resistance	>= 1000 hour	>= 1000 hour	F50, Condition C; ASTM D1693
Melt Flow	1.5 g/10 min	1.5 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	30	30	ASTM D2240
Tensile Strength, Ultimate	17.0 MPa	2470 psi	ASTM D638
Tensile Strength, Yield	9.00 MPa	1310 psi	ASTM D638
Elongation at Break	1300 %	1300 %	ASTM D638
Flexural Modulus	0.0920 GPa	13.3 ksi	1% Secant, ASTM D790
Tensile Impact Strength	3.80 kJ/m²	1.81 ft-lb/in²	23°C; ASTM D-1822

Thermal Properties	Metric	English	Comments
Melting Point	98.0 °C	208 °F	Exxon Method
Brittleness Temperature	-69.0 °C	-92.2 °F	ASTM D746