- LyondellBasell Hifaxâ„¢ CA187 Thermoplastic Olefin Resin
LyondellBasell Hifaxâ„¢ CA187 Thermoplastic Olefin Resin
| Category | Polymer , Thermoplastic |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CA187 Thermoplastic Olefin Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: medium melt flow, medium modulus, paintable thermoplastic elastomeric olefin resin, excellent paintability, excellent surface appearance, good impact and stiffness balanceApplications: painted automotive bumper fasciasDescription: Hifax CA187 medium melt flow, paintable thermoplastic elastomeric olefin resin has an excellent combination of processability and painability. It was designed primarily for painted automotive bumper fascia applications.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Tool, Montell |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO R527-1 |
| Elongation at Break | 450 % | 450 % | ISO R527-1 |
| Elongation at Yield | 11 % | 11 % | ISO R527-1 |
| Flexural Modulus | 0.830 GPa | 120 ksi | ISO 178 |
| Izod Impact, Notched | 0.220 J/cm @Temperature -40.0 °C |
0.412 ft-lb/in @Temperature -40.0 °F |
ISO 180 |
| Impact Test | 25.0 J @Temperature -30.0 °C |
18.4 ft-lb @Temperature -22.0 °F |
MAII, E at Max Load, Ductile; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature -30.0 - 100 °C |
55.6 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | ISO 75 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 0650-xx01D Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Edgetek® XT XT-100-CX01 PC+PBT (discontinued **)
- SABIC Innovative Plastics Lexan® FXD144R PC (Europe-Africa-Middle East)
- LyondellBasell Hifaxâ„¢ RTA3263/2 Thermoplastic Polyolefin Elastomer
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Polyfil HG90 Filler
- Lubrizol ESTALOC® 59300 Ester-Type, Reinforced Engineering Thermoplastic (European Grade)
- 3M 99786 Double Coated Tapes with 3M™ Adhesive 300MP
Copyright © lookpolymers.com All Rights Reserved