Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 7318 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE D 4201 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
Arlon A3020-B004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
Arlon A3020-T002-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
Arlon A3020-T004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 5003 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 2 hours at 177°C; ASTM D412 |
Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 4 hours at 177°C; ASTM D412 |
Multibase C6-515 Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Sylvin Technologies 8950-60 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Sylvin Technologies 9950-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 8.30 MPa @Temperature 49.0 °C |
1200 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 8.30 MPa @Temperature 49.0 °C |
1200 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Dow Corning C6-135 ELASTOMER KIT Two-part, platinum-catalyzed (1:1 by weight), silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices, and fabricating extruded.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Dow Corning C6-250 ELASTOMER One-part, enhanced tear-resistant silicone elastomers; uncatalyzed (customer selects peroxide catalyst) elastomer materials designed for compounding into elastomer for part fabrication and medical d.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Dow Corning C6-265 ELASTOMER One-part, enhanced tear-resistant silicone elastomers; uncatalyzed (customer selects peroxide catalyst) elastomer materials designed for compounding into elastomer for part fabrication and medical d.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Dow Corning SILASTIC® FL 40-9201 A&B KIT 40 shore A 100% fluorinated liquid silicone rubber. Designed for effective manufacturing of automotive parts that must wistand harsh environment, such as fuel contact under extreme temperatures.Info.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | |
Dow DOWLEX™ 2503.10 Linear Low Density Polyethylene, Narrow MW Distribution DOWLEX® 2503.10 Polyethylene resin is a narrow molecular weight distribution copolymer designed as a superior processing resin. For very thin wall higher cavitation molding, this grade often is a p.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | |
Dow LDPE 959I Low Density Polyethylene DOW LDPE 959I resin is a medium molecular weight distribution homo polymer designed to offer excellent clarity and flexibility with low warpage for lids. This resin has good processability over a wi.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4640 Dense Extruded Profile FormulationNordel® IP 4640 |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Dow Corning 25150-G SILICONE RUBBER Peroxide cured, general purpose silicone rubber compoundInformation provided by Dow Corning |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D638 |
Colorite Polymers 87-638A General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
3M 5360K Silicone Rubber Termination Kits 3M™ 5630K and 5690K Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Tape Shield, Wire Shield and UniShield® power cables. They meet the requireme.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42-68 |
3M 5600 Cold Shrink Silicone Rubber Termination Kits QT-III 3M™ Cold Shrink 5600 and 5680 Series QT-II Termination Kits contain one-piece silicone rubber terminations designed for concentric neutral (CN) cable. They meet the requirements of IEEE 48-1990 for.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
3M 5640 Silicone Rubber Termination Kits 3M™ 5640 and 5650 Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Jacketed Concentric Neutral (JCN) power cable. They meet the requirements of IEE.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42-68 |
3M 5680 Cold Shrink Silicone Rubber Termination Kits QT-III 3M™ Cold Shrink 5600 and 5680 Series QT-II Termination Kits contain one-piece silicone rubber terminations designed for concentric neutral (CN) cable. They meet the requirements of IEEE 48-1990 for.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D412; ISO 37 |
Advanced Polymer Alloys Alcryn® 3055 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | After 7 days at 257°F (125°C); ASTM D573; ISO 188 |
Advanced Polymer Alloys Alcryn® 4660 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D638 |
Colorite Polymers 5002 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Resinlab® EP1112 Black Electronic Grade Epoxy Encapsulant Resinlab™ EP 1112 Black is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. It cures completely at room temperature to a tough, flexib.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D412 |
G-2703 Styrene-based Biomedical Elastomer |