Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Relative, molded-without post cure; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 54
54
molded- without post cure; ASTM D2240
66
66
post cured- 2 hours at 177°C; ASTM D2240
67
67
post cured- 4 hours at 177°C; ASTM D2240
68
68
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 7.58 MPa
1100 psi
post cured- 4 hours at 177°C; ASTM D412
7.58 MPa
1100 psi
post cured- 8 hours at 177°C; ASTM D412
7.58 MPa
1100 psi
molded-without post cure; ASTM D412
8.27 MPa
1200 psi
post cured- 2 hours at 177°C; ASTM D412
Tensile Strength, Yield 1.86 MPa
270 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
2.69 MPa
390 psi
at 200%, molded-without post cure; ASTM D412
3.31 MPa
480 psi
200%, post cured- 4 hours at 177°C; ASTM D412
3.52 MPa
510 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 480 %
480 %
post cured- 8 hours at 177°C; ASTM D412
520 %
520 %
post cured- 4 hours at 177°C; ASTM D412
560 %
560 %
post cured- 2 hours at 177°C; ASTM D412
590 %
590 %
molded-without post cure; ASTM D412
Tear Strength 31.6 kN/m
180 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
35.1 kN/m
200 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
36.8 kN/m
210 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
36.8 kN/m
210 pli
Die B,molded-without post cure; ASTM D624
Compression Set 81 %
81 %
22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395
87 %
87 %
22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395
92 %
92 %
22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395
97 %
97 %
22 hours at 177°C, molded-without post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 2.50 %

@Temperature 177 °C,
Time 14400 sec
 2.50 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
2.50 %

@Temperature 177 °C,
Time 28800 sec
 2.50 %

@Temperature 351 °F,
Time 8.00 hour
 post cured
2.60 %

@Temperature 177 °C,
Time 7200 sec
 2.60 %

@Temperature 351 °F,
Time 2.00 hour
 post cured