- Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer
Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Multibase
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 35 | 35 | molded- without post cure; ASTM D2240 |
| 41 | 41 | post cured- 2 hours at 177°C; ASTM D2240 | |
| 41 | 41 | post cured- 4 hours at 177°C; ASTM D2240 | |
| 44 | 44 | post cured- 8 hours at 177°C; ASTM D2240 | |
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | molded-without post cure; ASTM D412 |
| 7.58 MPa | 1100 psi | post cured- 2 hours at 177°C; ASTM D412 | |
| 7.58 MPa | 1100 psi | post cured- 4 hours at 177°C; ASTM D412 | |
| 8.27 MPa | 1200 psi | post cured- 8 hours at 177°C; ASTM D412 | |
| Tensile Strength, Yield | 1.03 MPa | 150 psi | at 200%, molded-without post cure; ASTM D412 |
| 1.45 MPa | 210 psi | 200%, post cured- 4 hours at 177°C; ASTM D412 | |
| 1.45 MPa | 210 psi | at 200%, post cured- 2 hours at 177°C; ASTM D412 | |
| 1.79 MPa | 260 psi | 200%, post cured- 8 hours at 177°C; ASTM D412 | |
| Elongation at Break | 700 % | 700 % | post cured- 8 hours at 177°C; ASTM D412 |
| 750 % | 750 % | post cured- 4 hours at 177°C; ASTM D412 | |
| 760 % | 760 % | post cured- 2 hours at 177°C; ASTM D412 | |
| 950 % | 950 % | molded-without post cure; ASTM D412 | |
| Tear Strength | 22.8 kN/m | 130 pli | Die B,molded-without post cure; ASTM D624 |
| 22.8 kN/m | 130 pli | Die B,post cured- 2 hours at 177°C; ASTM D624 | |
| 22.8 kN/m | 130 pli | Die B, post cured- 4 hours at 177°C; ASTM D624 | |
| 24.5 kN/m | 140 pli | Die B, post cured- 8 hours at 177°C; ASTM D624 | |
| Compression Set | 54 % | 54 % | 22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395 |
| 74 % | 74 % | 22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395 | |
| 86 % | 86 % | 22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage | 3.10 % @Temperature 177 °C, Time 7200 sec |
3.10 % @Temperature 351 °F, Time 2.00 hour |
post cured |
| 3.50 % @Temperature 177 °C, Time 14400 sec |
3.50 % @Temperature 351 °F, Time 4.00 hour |
post cured | |
| 3.70 % @Temperature 177 °C, Time 28800 sec |
3.70 % @Temperature 351 °F, Time 8.00 hour |
post cured |