Multibase C6-250 PERKADOX PD-50S Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-250 PERKADOX PD-50S Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Relative, molded-without post cure; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 44
44
molded- without post cure; ASTM D2240
46
46
post cured- 4 hours at 177°C; ASTM D2240
49
49
post cured- 2 hours at 177°C; ASTM D2240
50
50
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 8.27 MPa
1200 psi
molded-without post cure; ASTM D412
8.27 MPa
1200 psi
post cured- 2 hours at 177°C; ASTM D412
8.96 MPa
1300 psi
post cured- 8 hours at 177°C; ASTM D412
9.65 MPa
1400 psi
post cured- 4 hours at 177°C; ASTM D412
Tensile Strength, Yield 2.28 MPa
330 psi
at 200%, molded-without post cure; ASTM D412
2.55 MPa
370 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
2.69 MPa
390 psi
200%, post cured- 4 hours at 177°C; ASTM D412
2.69 MPa
390 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 530 %
530 %
post cured- 8 hours at 177°C; ASTM D412
530 %
530 %
post cured- 2 hours at 177°C; ASTM D412
550 %
550 %
post cured- 4 hours at 177°C; ASTM D412
560 %
560 %
molded-without post cure; ASTM D412
Tear Strength 24.5 kN/m
140 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
26.3 kN/m
150 pli
Die B,molded-without post cure; ASTM D624
26.3 kN/m
150 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
26.3 kN/m
150 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
Compression Set 61 %
61 %
22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395
63 %
63 %
22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395
73 %
73 %
22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395
96 %
96 %
22 hours at 177°C, molded-without post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 2.00 %

@Temperature 177 °C,
Time 7200 sec
 2.00 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
2.20 %

@Temperature 177 °C,
Time 14400 sec
 2.20 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
2.30 %

@Temperature 177 °C,
Time 28800 sec
 2.30 %

@Temperature 351 °F,
Time 8.00 hour
 post cured