- Polymer Property : Tensile Strength, Ultimate = 8.27 MPa
Polymer Property : Tensile Strength, Ultimate = 8.27 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Resinlab® EP1112 Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP 1112 Clear is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. It cures completely at room temperature to a tough, flexib.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 2 hours at 177°C |
| Multibase SILASTIC® C7-4565 TBPB Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
| Arlon A3020-B004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
| Arlon A3020-T004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 8 hours at 177°C; ASTM D412 |
| Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | molded-without post cure; ASTM D412 |
| Multibase C6-250 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 4 hours at 177°C; ASTM D412 |
| Multibase C6-250 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | molded-without post cure; ASTM D412 |
| Multibase C6-250 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 2 hours at 177°C; ASTM D412 |
| Multibase C6-250 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 8 hours at 177°C; ASTM D412 |
| Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 2 hours at 177°C; ASTM D412 |
| Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 4 hours at 177°C; ASTM D412 |
| Multibase C6-515 Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Sylvin Technologies 8950-60 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Sylvin Technologies 9077-85 LMW Natural PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Sylvin Technologies 9950-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Dow Corning C6-265 ELASTOMER One-part, enhanced tear-resistant silicone elastomers; uncatalyzed (customer selects peroxide catalyst) elastomer materials designed for compounding into elastomer for part fabrication and medical d.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Dow Corning SILASTIC® FL 40-9201 A&B KIT 40 shore A 100% fluorinated liquid silicone rubber. Designed for effective manufacturing of automotive parts that must wistand harsh environment, such as fuel contact under extreme temperatures.Info.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D638 |
| Colorite Polymers 87-638A General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42-68 |
| 3M 4605 Silicone Rubber Termination Kit 3M™ 4604 and 4605 Quick Term II Silicone Rubber Termination Kits are three-piece Cold Shrink terminations for Tape Shield, Wire Shield, and LC Shield power cables. They meet the requirements of IEE.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
| 3M 5360K Silicone Rubber Termination Kits 3M™ 5630K and 5690K Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Tape Shield, Wire Shield and UniShield® power cables. They meet the requireme.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
| 3M 5640 Silicone Rubber Termination Kits 3M™ 5640 and 5650 Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Jacketed Concentric Neutral (JCN) power cable. They meet the requirements of IEE.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
| 3M 5650 Silicone Rubber Termination Kits 3M™ 5640 and 5650 Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Jacketed Concentric Neutral (JCN) power cable. They meet the requirements of IEE.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
| 3M 5690K Silicone Rubber Termination Kits 3M™ 5630K and 5690K Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Tape Shield, Wire Shield and UniShield® power cables. They meet the requireme.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D412; ISO 37 |
| Advanced Polymer Alloys Alcryn® 3055 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | After 7 days at 257°F (125°C); ASTM D573; ISO 188 |
| Advanced Polymer Alloys Alcryn® 4660 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D638 |
| Colorite Polymers 5002 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42-68 |
| 3M 4604 Silicone Rubber Termination Kit 3M™ 4604 and 4605 Quick Term II Silicone Rubber Termination Kits are three-piece Cold Shrink terminations for Tape Shield, Wire Shield, and LC Shield power cables. They meet the requirements of IEE.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
| Resinlab® EP1112 Black Electronic Grade Epoxy Encapsulant Resinlab™ EP 1112 Black is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. It cures completely at room temperature to a tough, flexib.. |
|||
| Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D412 |
| G-2703 Styrene-based Biomedical Elastomer |
|||