Polymer Property : Tensile Strength, Ultimate = 8.30 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	8.30 MPa	1200 psi	ASTM D412
Multibase Multi-Flex® TPE A 7318 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	8.30 MPa	1200 psi	ASTM D412
Multibase Multi-Flex® TPE D 4201 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	8.30 MPa	1200 psi	ASTM D412
Multibase Multi-Flex® TPE G 7455 BLK Flame retardant thermoplastic rubber based on Shell's Kraton G polymers, manufactured under Shell's license. Product exhibits VO rating. Multi-Flex TPE contains Kraton™ G.Data provided by Multiba..
Tensile Strength, Ultimate	8.30 MPa	1200 psi	ASTM D412
Multibase Multi-FlexÂ® TPE A 5003 BLK Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
Tensile Strength, Ultimate	8.30 MPa @Temperature 49.0 °C	1200 psi @Temperature 120 °F	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	8.30 MPa @Temperature 49.0 °C	1200 psi @Temperature 120 °F	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	8.30 MPa	1200 psi	ASTM D638/D412
Covestro Baydur® 646 Polyurethane Structural Foam RIM, Density 25 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of..
Tensile Strength, Ultimate	8.30 MPa	1200 psi
Dow DOWLEX™ 2503.10 Linear Low Density Polyethylene, Narrow MW Distribution DOWLEX® 2503.10 Polyethylene resin is a narrow molecular weight distribution copolymer designed as a superior processing resin. For very thin wall higher cavitation molding, this grade often is a p..
Tensile Strength, Ultimate	8.30 MPa	1200 psi
Dow LDPE 959I Low Density Polyethylene DOW LDPE 959I resin is a medium molecular weight distribution homo polymer designed to offer excellent clarity and flexibility with low warpage for lids. This resin has good processability over a wi..
Tensile Strength, Ultimate	8.30 MPa	1200 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4640 Dense Extruded Profile FormulationNordel® IP 4640
Tensile Strength, Ultimate	8.30 MPa	1200 psi	ASTM D638
Buckeye Polymers BP Flex A9008 TPO TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resistance and have a..