Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 64
64
molded- without post cure; ASTM D2240
70
70
post cured- 4 hours at 177°C; ASTM D2240
71
71
post cured- 2 hours at 177°C; ASTM D2240
73
73
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 7.58 MPa
1100 psi
molded-without post cure; ASTM D412
7.58 MPa
1100 psi
post cured- 2 hours at 177°C; ASTM D412
7.58 MPa
1100 psi
post cured- 4 hours at 177°C; ASTM D412
8.27 MPa
1200 psi
post cured- 8 hours at 177°C; ASTM D412
Tensile Strength, Yield 3.03 MPa
440 psi
at 200%, molded-without post cure; ASTM D412
4.14 MPa
600 psi
200%, post cured- 4 hours at 177°C; ASTM D412
4.21 MPa
610 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
4.55 MPa
660 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 430 %
430 %
post cured- 8 hours at 177°C; ASTM D412
430 %
430 %
post cured- 2 hours at 177°C; ASTM D412
450 %
450 %
post cured- 4 hours at 177°C; ASTM D412
620 %
620 %
molded-without post cure; ASTM D412
Tear Strength 33.3 kN/m
190 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
33.3 kN/m
190 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
35.1 kN/m
200 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
40.3 kN/m
230 pli
Die B,molded-without post cure; ASTM D624
Compression Set 52 %
52 %
22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395
74 %
74 %
22 hours at 177°C, molded-without post cure; ASTM D395
83 %
83 %
22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395
91 %
91 %
22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 2.70 %

@Temperature 177 °C,
Time 14400 sec
 2.70 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
3.20 %

@Temperature 177 °C,
Time 7200 sec
 3.20 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
3.20 %

@Temperature 177 °C,
Time 28800 sec
 3.20 %

@Temperature 351 °F,
Time 8.00 hour
 post cured