Multibase C6-250 DI-CUP R Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-250 DI-CUP R Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 48
48
molded- without post cure; ASTM D2240
55
55
post cured- 2 hours at 177°C; ASTM D2240
55
55
post cured- 4 hours at 177°C; ASTM D2240
57
57
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 8.27 MPa
1200 psi
molded-without post cure; ASTM D412
8.27 MPa
1200 psi
post cured- 4 hours at 177°C; ASTM D412
8.96 MPa
1300 psi
post cured- 8 hours at 177°C; ASTM D412
8.96 MPa
1300 psi
post cured- 2 hours at 177°C; ASTM D412
Tensile Strength, Yield 2.28 MPa
330 psi
at 200%, molded-without post cure; ASTM D412
3.10 MPa
450 psi
200%, post cured- 4 hours at 177°C; ASTM D412
3.10 MPa
450 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
3.45 MPa
500 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 460 %
460 %
post cured- 8 hours at 177°C; ASTM D412
480 %
480 %
post cured- 4 hours at 177°C; ASTM D412
490 %
490 %
post cured- 2 hours at 177°C; ASTM D412
610 %
610 %
molded-without post cure; ASTM D412
Tear Strength 24.5 kN/m
140 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
29.8 kN/m
170 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
29.8 kN/m
170 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
36.8 kN/m
210 pli
Die B,molded-without post cure; ASTM D624
Compression Set 50 %
50 %
22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395
62 %
62 %
22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395
67 %
67 %
22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395
67 %
67 %
22 hours at 177°C, molded-without post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 2.90 %

@Temperature 177 °C,
Time 14400 sec
2.90 %

@Temperature 351 °F,
Time 4.00 hour
post cured
3.00 %

@Temperature 177 °C,
Time 7200 sec
3.00 %

@Temperature 351 °F,
Time 2.00 hour
post cured
3.40 %

@Temperature 177 °C,
Time 28800 sec
3.40 %

@Temperature 351 °F,
Time 8.00 hour
post cured