Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
North Wood Plastics Polypropylene with 40% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
Density | 1.02 - 1.02 g/cc @Temperature 280 - 300 °C |
0.0368 - 0.0368 lb/in³ @Temperature 536 - 572 °F |
Average value: 1.02 g/cc Grade Count:6 |
Overview of materials for Polycarbonate, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Impact Modified". Each property range of values reported is minimum and maximum values of.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Solvay Chemicals NOCOLOK® Binder (water-based) Binder to reduce flux fall-off and minimize dust formationUses: Automotive Sector, Commercial & Residential Air Conditioning, Refrigeration and Household & Electrical AppliancesInformation provided.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
Styrolution Terluran® HI-12 ABS Terluran HI-12 is an injection molding grade of ABS with a very high toughness and easy flow.Very high toughnessEasy flowingUL 94 HB (1.6 & 3.2 mm)Information provided by Styrolution |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Solvay ALKAMULS® A 9 Surfactant Identification: ETHOXYLATED OLEIC ACIDCAS: 9004 – 96 – 0Available in: Asia Pacific, Europe, Latin America and North America Solubility: Dispersible in water. Soluble in most polar and arom.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Solvay GERONOL® MS Surfactant Description: Multipurpose emulsifier for EC, to use in pair with Geronol FF/4 or Rhodacal 70/B.Identification: BLENDED EMULSIFIERSSolubility: Soluble in water and most polar and aromatic solventsAva.. |
|||
Density | 1.02 - 1.04 g/cc | 0.0368 - 0.0376 lb/in³ | approximation |
Struktol STRUKSILON 8101 Silicone Stabilizer for PU-Rigid Foam STRUKSILON 8101 is used as a silicone stabilizer for production of polyurethane rigid foam. It is especially recommended for the use in PU-1- or PU-2-component spray foam applications.Applications: .. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Sax Polymers SAXLAC 207 Acrylonitrile Butadiene Styrene Saxalac 207 is a high heat ABS, characterized by high impact strength and high stiffness.Mechanical property data tested at 50% RH.Information provided by SAX Polymers |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Sax Polymers SAXLAC 310A Acrylonitrile Butadiene Styrene Saxalac 310A is a medium viscosity, impact resistant ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provid.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
UBE UBESTA® 3024U Rigid Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
Polyplastics TOPAS® 5013 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade) This grade is characterized by its high flowability and superior optical properties. It is suitable for optical components such as lenses and light guide panels where high molded precision is indisp.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
Polyplastics TOPAS® 6017 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade) Possesses the highest heat resistance among cyclic olefin-type resins.Information provided by PolyPlastics. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Loctite® 554 Refrigerant Sealant Thread Sealant Thread SealersLoctite® Liquid Thread Sealants seal and secure metal pipes and fittings, filling the space between threaded metal parts, and hardening to prevent leakage. Designed for low and high p.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | Melt |
Covestro Desmopan® DP 3690AU Polyurethane Extrusion- and injection molding gradehydrolysis-stabilisedwith special UV stabilizerswith release agenttransparent up to 6 mm wall thicknessgood wear resistanceApplicationSports shoe solesFilmsHose.. |
|||
Density | 1.02 g/cc @Temperature 300 °C |
0.0368 lb/in³ @Temperature 572 °F |
Melt |
Covestro Makrolon® 2806 Polycarbonate ISO 7391-PC,M,(,,)-09-9MVR (300 °C/1.2 kg) 9.5 cm3/10 minFood contact qualityMedium viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAvailable in transparenttran.. |
|||
Density | 1.02 g/cc @Temperature 290 °C |
0.0368 lb/in³ @Temperature 554 °F |
Melt |
Covestro Makrolon® AG2677 Polycarbonate ISO 7391-PC,MLR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minMedium viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transparent colors on.. |
|||
Density | 1.02 g/cc @Temperature 290 °C |
0.0368 lb/in³ @Temperature 554 °F |
Melt |
Covestro Makrolon® T7855 Polycarbonate, Impact Grade ISO 7391-PC,MPR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12 cm3/10 minImpact modifiedMedium viscosityEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in opaque colors onlyPre.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
DuPont Performance Polymers Hytrel® 4056 Polyester Elastomer TPC-ET
(Unverified Data**) 40 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers |
|||
Density | 1.02 g/cc @Temperature 300 °C |
0.0368 lb/in³ @Temperature 572 °F |
Melt |
Covestro Makrolon® LQ3187 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minOptical lensHigh viscosityUV stabilizedUV 400 cut offEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable i.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ISO R1183 |
Arkema Group Orgalloy® LE 60 LM Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Arkema Group Pebax® 7233 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 72 shore D Highest modulus PEBAX Applications: medical, extrusion SportISO data provided by the manufacturer, Arkema. |
|||
Density | 1.02 - 1.05 g/cc | 0.0368 - 0.0379 lb/in³ | |
BASF Styropor® F 215 N Expandable Polystyrene Description: Expandable polystyrene (EPS) containing a uniformly distributed ?ame retardant (blowing agent: pentane)Remarks: For the manufacture of flame-retardant foams.Applications: Blocks, insula.. |
|||
Density | 1.02 - 1.05 g/cc | 0.0368 - 0.0379 lb/in³ | |
BASF Styropor® F 315-N Expandable Polystyrene Description: Expandable polystyrene (EPS) containing uniformly distributed flame retardant (blowing agent: pentane)Remarks: Production of flame-retardant foams displaying low post-shrinkageApplicati.. |
|||
Density | 1.02 - 1.05 g/cc | 0.0368 - 0.0379 lb/in³ | |
BASF Styropor® P 570 Expandable Polystyrene Additive Description: Expandable polystyrene (EPS) (blowing agent: pentane).Remarks: Only foamed particles, good foaming capacity.Applications: For the production of expanded particles as a filling material .. |
|||
Density | 1.02 - 1.05 g/cc | 0.0368 - 0.0379 lb/in³ | |
BASF Styropor® F 295-N Expandable Polystyrene Description: Expandable polystyrene (EPS) containing uniformly distributed flame retardant (blowing agent: pentane)Remarks: Production of flame-retardant foams displaying low post-shrinkageApplicati.. |
|||
Density | 1.02 - 1.05 g/cc | 0.0368 - 0.0379 lb/in³ | |
BASF Styropor® P 656 Expandable Polystyrene Additive Description: Expandable polystyrene (EPS) (blowing agent: pentane).Remarks: Only foamed particles, good foaming capacity.Applications: Filling material for lightweight plasters.Information provided .. |
|||
Density | 1.02 - 1.05 g/cc | 0.0368 - 0.0379 lb/in³ | |
BASF Neopor® 2200 Expandable Polystyrene Description: Expandable polystyrene (EPS) containing uniformly distributed flame retardant (blowing agent: pentane).Remarks: For the production of flame-retardant silver-gray foams having a consider.. |
|||
Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
DuPont Conpol™ 20LO Ethylene-Methacrylic Acid Additive Resin
(discontinued **) Conpol™ additive resins, supplied in pellet form, are designed to modify the surface properties of films or coatings of Surlyn® ionomer resins and Nucrel® acid copolymer resins. They are concentr.. |