Wellman Wellamid® XT1486-BK Medium Impact Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® XT1486-BK Medium Impact Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Medium Impact Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage, Flow | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527-93 |
| Elongation at Break | 50 % | 50 % | ISO 527-93 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178-93 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 13.5 kJ/m² | 6.42 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 277 - 293 °C | 530 - 560 °F | |
| Middle Barrel Temperature | 271 - 288 °C | 520 - 550 °F | |
| Front Barrel Temperature | 266 - 282 °C | 510 - 540 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 271 - 304 °C | 520 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |
Users viewing this material also viewed the following:
- Mallard Creek Polymers TYLAC® 812 SBR Emulsion
- Lubriplate SPO-266 Petroleum-Based Gear, Bearing, & Recirculating Oil
- Lubriplate Super GPO L0754 Heavy-Duty Motor Oil Motor Oil & Transmission Fluid
- Lubrizol Advanced Materials PEARLBOND® 106 Linear Thermoplastic Polyurethane
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours
- Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F)
- Total PPH 3825WZ Polypropylene, Injection Molding Grade
- Eifeler Coatings Technology TOPMATIC TiAlN PVD Coating
- ChevronTexaco HDAX® SAE 40 Low Ash Gas Engine Oil
- BASF Ultraform® FK 66003 20% Silicone Filled POM
Copyright © lookpolymers.com All Rights Reserved