EMS-Grivory Grivory® GV-6H EF black 9915 PA*-GF60

Category	Polymer , Thermoplastic , Nylon
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® GV-6H EF black 9915 PA*-GF60.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product description: Grivory GV-6H black 9915 is a 60% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copolyamide. Grivory GV-6H black 9915 is used for injection molding technical parts, exhibiting exceptional characteristics even after moisture absorption: high stiffness and strengthdimensional stability, low warpagegood chemical resistancegood surface finish Grivory GV is the economical alternative to die-cast alloys.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.69 g/cc	0.0611 lb/in³	ISO 1183
Water Absorption	3.5 %	3.5 %	ISO 62
Moisture Absorption	1.20 %	1.20 %	ISO 62
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0030 cm/cm	0.0030 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	290 MPa	42100 psi	conditioned; ISO 2039-1
	315 MPa	45700 psi	dry; ISO 2039-1
Tensile Strength at Break	240 MPa	34800 psi	conditioned; ISO 527-1/-2
	260 MPa	37700 psi	dry; ISO 527-1/-2
Elongation at Break	2.0 %	2.0 %	dry; ISO 527-1/-2
	2.0 %	2.0 %	conditioned; ISO 527-1/-2
Tensile Modulus	21.0 GPa	3050 ksi	conditioned; ISO 527-1/-2
	22.0 GPa	3190 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	8.00 J/cm²	38.1 ft-lb/in²	dry; ISO 179/1eU
	8.00 J/cm²	38.1 ft-lb/in²	conditioned; ISO 179/1eU
	8.00 J/cm² @Temperature 30.0 °C	38.1 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	8.00 J/cm² @Temperature 30.0 °C	38.1 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	1.40 J/cm²	6.66 ft-lb/in²	dry; ISO 179/1eA
	1.40 J/cm²	6.66 ft-lb/in²	conditioned; ISO 179/1eA
	1.30 J/cm² @Temperature 30.0 °C	6.19 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	1.30 J/cm² @Temperature 30.0 °C	6.19 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 µm/m-°C	8.33 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	90.0 µm/m-°C	50.0 µin/in-°F	ISO 11359-1/-2
Melting Point	260 °C	500 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	100 - 120 °C	212 - 248 °F	long term; EMS
	220 °C	428 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	235 °C	455 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	175 °C	347 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	dry; IEC 60093
	1.00e+14 ohm-cm	1.00e+14 ohm-cm	conditioned; IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Strength	33.0 kV/mm	838 kV/in	dry; IEC 60243-1
	33.0 kV/mm	838 kV/in	conditioned; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
	Compressed air systems
	Cooling and climate control
	Exterior
	Fuel systems
Electricals & Electronics	Connectors
	Electrical appliances
	Electrical equipment
	Energy distribution
	Lighting
	Mobile phones and other portable devices
Form	Granules
Processing	Injection Molding
Product Attributes	Barrier Properties
	Co Polyamide
	High viscosity
	Long Fiber Reinforced
	Masterbatch
	Nucleated
	Transparent Polyamide