- Suzhou Hipro Polymers Hiprolon® 200 MC HLS G30 Nylon 1010, 30% glass fiber filled
Suzhou Hipro Polymers Hiprolon® 200 MC HLS G30 Nylon 1010, 30% glass fiber filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Suzhou Hipro Polymers |
| Trade Name | Hiprolon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Suzhou Hipro Polymers Hiprolon® 200 MC HLS G30 Nylon 1010, 30% glass fiber filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hiprolon® 200 MC HLS G30 is a polyamide 10.10 compound reinforced with 30% chopped glass fiber for injection molding; features high dimension stability, chemical resistance, impact resistance, low friction, high flow ability; widely used for auto parts, thin wall housing, machinery & sports equipment et al;Information provided by Suzhou Hipro Polymers Co. Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | normal; ISO 294-4,2577 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | ISO 294-4,2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 136 MPa | 19700 psi | ISO527-2/1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 9.50 J/cm² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.90 J/cm² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 202 °C | 396 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75-1/2 |
| Vicat Softening Point | 190 °C | 374 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC60695 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ISO 60695 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 290 °C | 464 - 554 °F | |
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 130 MPa | 10200 - 18900 psi |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_9110/9410/9210/9310 Rubber-like Prototyping Polymer
- SABIC Innovative Plastics Cycoloy® RCY6013 PC+ABS (Asia Pacific)
- Solvay Specialty Polymers Halar® 9414 Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)&l
- Latrobe Lescalloy® AF 1410 VIM-VAR ; 9 in High Strength Alloy Steel
- Ecomass® 1002ZC85 Stainless Steel Filled COPA
- DuPont Performance Polymers Neoprene GNA Polychloroprene
- DuPont Teijin Films Mylar® ADS Polyester Film, 300 Gauge
- 3M CN-3490 EMI Shielding Tape
- Applied Composites 8041 Polyester SMC
- Parker Chomerics CHO-FORM 5528 Conductive Form-In-Place Gaskets
Copyright © lookpolymers.com All Rights Reserved