- Styrolution Luran® 348 Q Crystal Clear Transparent 77850 SAN
Styrolution Luran® 348 Q Crystal Clear Transparent 77850 SAN
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Transparent |
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Luran® 348 Q Crystal Clear Transparent 77850 SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Highly transparent grade with low natural color.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | |
| Melt Flow | 20.52 g/10 min @Load 10.0 kg, Temperature 220 °C |
20.52 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| 29.16 g/10 min @Load 21.6 kg, Temperature 200 °C |
29.16 g/10 min @Load 47.6 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 77 | 77 | ISO 2039-2 |
| Ball Indentation Hardness | 160 MPa @Load 36.5 kg, Time 30.0 sec |
23200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527-1/-2 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.50 kJ/m² | 0.714 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.150 J/cm² @Temperature 23.0 °C |
0.714 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75-1/-2 |
| Vicat Softening Point | 105 °C | 221 °F | VST B50; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Pre-drying |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Transparent 77850 | |
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Plaskolite Optix® CP - 927 GHF High Impact Grade Acrylic Resin
- Dielectric Polymers NT-140A89 General Purpose Laminating Adhesive (discontinued **)
- PolyOne Stat-Tech™ AS-15CP/000 ABS - 15% Carbon Powder (discontinued **)
- Hybrid Plastics CO6U50.02 Nanoreinforced® Cyclic Olefin Copolymer
- SABIC Innovative Plastics NORYL GTX GTX8730 PPE+PA
- DSM Arnitel® PB582-H 58 Shore D, Blow Molding Grade, Heat Stabilized Copolyester Elastomer (North America)
- China Tungsten ST1365 PM Antifriction Parts
- Arlon 51576R015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR MBT
Copyright © lookpolymers.com All Rights Reserved