SABIC Innovative Plastics LNP STAT-KON DFD03 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DFD03 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.230 % | 0.230 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 |
| 6.30 GPa | 914 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 140 MPa | 20300 psi | ISO 178 | |
| Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.48 GPa | 795 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.55 GPa | 805 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.74 J/cm | 10.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.67 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 7.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
3.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 4.0 - 6.0 ohm | 4.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Polymist® F-5 PTFE Powder Lubricant (discontinued **)
- SMAC SMACTANE® 50 1114S- N03 Damping Material
- ExxonMobil Gargoyle Arctic 234 SHC 200 Series
- E-Polymers SEPAZ® V235A 35% Glass Fiber Reinforced PPA
- Colorite Polymers Vinylbond 6527P-MD Grey 499 Compound
- Akzo Nobel Trigonox® C-C75 Polymerization Initiator
- BASF Pluracol® 4650 Graft Slabstock Foam Polyol
- Sinotek Materials Packing Expanded Graphite Braided
Copyright © lookpolymers.com All Rights Reserved