- Polymer Property : Tensile Strength at Break = 70.0 MPa
Polymer Property : Tensile Strength at Break = 70.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO.527 DIN.53455 |
| Omnia Plastica PSU Polysulphone It is a non-reinforced amorphous polymer whose main features are its high thermal, electrical and mechanical properties which are typical of a crystalline polymer. Compared to its "brother" PES it h.. |
|||
| Tensile Strength at Break | <= 70.0 MPa | <= 10200 psi | ISO/R527 |
| Polykemi AB POLYfill PPH GF5030 PB Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Nilit FRIANYL A63 S10 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® 101R PC (Europe-Africa-Middle East) LEXAN 101R is a high viscosity multi purpose grade and contains a release agent to ensure easy processing. LEXAN 101R is available in transparent, translucent and opaque colours. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® 104R PC UL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. Internal mold release. FDA food contact compliant in limited colors.Effective January 15.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® AD143 PC (Europe-Africa-Middle East) LEXAN AD143 is a medium viscosity, injection molding grade exhibiting low dust attraction. It is designed for applications with high optical requirements in terms of clarity and light transmission .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXD103R PC (Asia Pacific) FXD103R is a Light Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect propert.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXD104R PC (Europe-Africa-Middle East) FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HP6REU PC (Europe-Africa-Middle East) Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® IR2840 PC 7.0 MFR, for thicker sections without sinks. Internal mold release. FDA food contact compliant, natural only.Effective January 15th, 2007 this grade will no longer be supported with biocompatibilit.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® OQ3732 PC (Europe-Africa-Middle East) High Viscosity, UV-stabilized PC for ophthalmic lenses. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EX1632T PC (Europe-Africa-Middle East) LEXAN* EX1632T polycarbonate resin, MVR (300C/1.2kg) 6 cm3/10min, high viscosity, branched, extrusion, mold release, UV stabilized, transparent, translucent and opaque colors. Multiwall sheet, Profi.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Nilit FRIANYL C73 M-HS3005 Nylon 6.6/6 for injection molding, 30% mineral filled Nylon 6.6/6 for injection molding, medium viscosity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXD104R PC (Asia Pacific) FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXM161R PC (Europe-Africa-Middle East) LEXAN FXM161R is a transparent/translucent medium viscosity grade for special effects colours with a metallic-luster appearance. Color package may affect performance.This data was supplied by SABIC-.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® SLX1231D PC Copolymer (Europe-Africa-Middle East) Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Grupo Repol Dinalon® B1S25 H PA6 Heat Stabilized Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Strength at Break | 70.0 MPa @Thickness 2.00 mm |
10200 psi @Thickness 0.0787 in |
ASTM D638 |
| Mitsui Arlen™ AE4200 Modified Nylon 6T, for Tribolic Applications (COND) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
| Tensile Strength at Break | 70.0 MPa @Thickness 2.00 mm |
10200 psi @Thickness 0.0787 in |
ASTM D638 |
| Mitsui Arlen™ AE4200N Modified Nylon 6T, for Tribolic Applications, Flame Retardant (DAM) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Lanxess Pocan® B 3215 XF 901510 PBT, 10% Glass Fiber PBT, 10% glass fibers, injection molding, improved flowability, impact modified |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | |
| LATI Latishield 38/11-08A G/10 ABS/PC, Steel/Glass Fiber Reinforced EMI shielding product based on ABS/PC Blend (ABS/PC). Steel fibers. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA 6/12 (Asia Pacific) LNP* LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50mm/min; ISO 527 |
| Teijin Panlite® G-3410R Glass Fiber Reinforced Polycarbonate Resin GF 10% reinforced and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machinery components th.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| DSM Akulon® K223-KMV6 (GREY) Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| DSM Stanyl® TW200FM33 Nylon 46-30% Glass and Mineral Reinforced (European Grade) (Cond) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® BK-30 PA6-GB30 Information provided by EMS Grivory |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Ascend Performance Materials Vydyne® 67B Nylon 66, General Purpose, very high viscosity, Conditioned Vydyne® 67B is a very-high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 67B resin offers high strength, rigidity and.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® SD1318 PC High viscosity, UV stabilized multi purpose grade. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO R 527 |
| Addiplast Addinyl B2 G30 Nylon 6, 30% Glass Bead Glass bead reinforced, improved stiffness and dimensional stabilityInformation provided by Addiplast. |
|||
| Tensile Strength at Break | <= 70.0 MPa | <= 10200 psi | ISO/R527 |
| Polykemi AB POLYfill PPC GF15030 PD1 VT2 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled, Heat Stabilized Information provided by Polykemi AB |
|||