- Polymer Property : Tensile Strength at Break = 10200 psi
Polymer Property : Tensile Strength at Break = 10200 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | |
| Plastcom SLOVASTER® B1 GF 6/2 PBT reinforced with 6% glass fibre Features: PBT for injection moulding, chemically reinforced with 6 % glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bendi.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1005 Resin. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® 164R PC (Europe-Africa-Middle East) Medium viscosity, multi purpose polycarbonate resin with added release agent. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with b.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® 241 PC (Europe-Africa-Middle East) LEXAN 241 resin is a medium viscosity multi purpose polycarbonate with UL94-V2 rated. All color options are available. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXE163R PC (Europe-Africa-Middle East) LEXAN FXE163R is a transparent/translucent UV stabilized, medium viscosity grade for special effects with fluorescent appearance. Color package may affect performance. LEXAN FXE163R contains a relea.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HP2EU PC (Europe-Africa-Middle East) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mol.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® IFX6420Z PC (Asia Pacific) Lexan* IFX6420Z is a medium viscosity, release containing, injection moldable, polycarbonate grade suitable for use in industry protective eye-ware welding applications. This grades meets the transm.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Americas regio.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® SLX2431D PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FST3403 PC Copolymer Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® SLX1231T PC Copolymer Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 70.3 MPa | 10200 psi | ASTM D638 |
| Solvay Specialty Polymers Udel® P-3500 LCD MB Polysulfone (PSU)
(Unverified Data**) Udel polysulfone is a tough, rigid, high-strength thermoplastic with outstanding hydrolytic resistance. Udel P-3500 LCD MB series polymers are particularly well suited for the fabrication of porous .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 - 1/2 |
| Hexion Bakelite™ EP 8414 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage
(dis Epoxy molding compound, inorganically filled, glass fiber reinforced, highly heat resistant, good electrical even at higher temperatures, very slight post shrinkage, increased media resistance, UL l.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| DSM Akulon® Ultraflow™ K-FHGM44 Nylon 6-40% Glass and Mineral Reinforced (European and Asian Grade) (Cond)
(d The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ASTM D638 |
| LG Chemical HP PMMA Information Provided by LG Chem |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Mitsubishi Xantar® SF 2230 Polycarbonate-30% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Grupo Repol Dinalon® B1S25 H PA6 Heat Stabilized Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | |
| LATI Laticonther 88/10 GR/50 PEEK, 50% Graphite Reinforced High thermal conductivity product based on Polyetheretherketone (PEEK). Graphite. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | |
| LATI Latiohm 90/13-09 PD01 G/10 PPOm, 10% Glass Fiber Reinforced Semiconductive/dissipative product based on Modified Polyphenylene Oxide (PPOm). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation prov.. |
|||
| Tensile Strength at Break | 70.3 MPa | 10200 psi | ASTM D638 |
| Solvay Specialty Polymers Udel® P-3500 LCD MB Polysulfone (PSU) Udel® polysulfone is a tough, rigid, high-strength thermoplastic with outstanding hydrolytic resistance. Udel® P-3500 LCD MB series polymers are particularly well suited for the fabrication of.. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Unitika A3130HR-25 PA6, 25% Mineral Reinforced, Dry Information provided by Unitika Ltd. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-93 |
| Wellman Wellamid® MR340 42H-NBK1 Nylon 6, 34% Mineral Reinforced All information provided by Wellman Engineered Resins. |
|||
| Tensile Strength at Break | 70.3 MPa | 10200 psi | ASTM D638 |
| A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 70.3 MPa | 10200 psi | ASTM D638 |
| A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Eurostar Starflam AFR682B1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding Starflam AFR682B1 is a Flame Retardant, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Eurostar Staramide ALY540A PA66, Glass/Mineral Fiber Reinforced, Injection Molding Staramide ALY540A is a Glass Fiber Reinforced, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength at Break | 70.0 MPa @Temperature 80.0 °C |
10200 psi @Temperature 176 °F |
ASTM Test |
| BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature
performance and .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 66J Nylon 66, General Purpose, high viscosity, Conditioned Vydyne® 66J is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66J resin offers high strength, .. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXM163R PC (Europe-Africa-Middle East) PC with Visual Effect, UV-Stabilizer, Heat Stabilized, Opaque. Colour package may affect properties. Application testing always recommended. |
|||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Styrolution Luran® 348 Q Crystal Clear Transparent 77850 SAN Description: Highly transparent grade with low natural color.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||