Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
Manufacturer | Solvay |
Trade Name | Technyl® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Solvay Technyl® A 402 H1 Nylon 66.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183-A |
Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ISO 62 |
Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | Rhodia EP test |
Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | Rhodia EP test |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 60.0 MPa | 8700 psi | DAM; ISO 527 Type 1 A |
Tensile Strength, Yield | 60.0 MPa | 8700 psi | Conditioned; ISO 527 Type 1 A |
80.0 MPa | 11600 psi | DAM; ISO 527 Type 1 A | |
Elongation at Break | 60 % | 60 % | DAM; ISO 527 Type 1 A |
250 % | 250 % | Conditioned; ISO 527 Type 1 A | |
Elongation at Yield | 8.0 % | 8.0 % | DAM; ISO 527 Type 1 A |
30 % | 30 % | Conditioned; ISO 527 Type 1 A | |
Tensile Modulus | 1.30 GPa | 189 ksi | Conditioned; ISO 527 Type 1 A |
3.10 GPa | 450 ksi | DAM; ISO 527 Type 1 A | |
Flexural Strength | 75.0 MPa | 10900 psi | Conditioned; ISO 178 |
140 MPa | 20300 psi | DAM; ISO 178 | |
Flexural Modulus | 1.30 GPa | 189 ksi | Conditioned; ISO 178 |
2.80 GPa | 406 ksi | DAM; ISO 178 | |
Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | DAM; ISO 180/A |
35.0 kJ/m² | 16.7 ft-lb/in² | Conditioned; ISO 180/A | |
Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU |
NB | NB | Conditioned; ISO 179/1eU | |
Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DAM; ISO 179/1eA |
3.00 J/cm² | 14.3 ft-lb/in² | Conditioned; ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
DAM; ISO 11359 |
Melting Point | 263 °C | 505 °F | ISO 11357 |
Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ISO 75-2 |
Oxygen Index | 27 % | 27 % | Dry; ISO 4589 |
Glow Wire Test | 775 °C @Thickness 1.60 mm |
1430 °F @Thickness 0.0630 in |
Ignition Temperature; DAM; IEC 60695-2-13 |
775 °C @Thickness 3.20 mm |
1430 °F @Thickness 0.126 in |
Ignition Temperature; DAM; IEC 60695-2-13 | |
960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Flammability Index; DAM; IEC 60695-2-12 | |
960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
Flammability Index; DAM; IEC 60695-2-12 | |
960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Flammability Index; DAM; IEC 60695-2-12 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; IEC 60093 |
1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DAM; IEC 60093 | |
Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | Conditioned; IEC 60093 |
1.00e+12 ohm | 1.00e+12 ohm | DAM; IEC 60093 | |
Dielectric Strength | 26.0 kV/mm | 660 kV/in | Conditioned; IEC 60243 |
27.0 kV/mm | 686 kV/in | DAM; IEC 60243 | |
Dissipation Factor | 0.020 | 0.020 | DAM; IEC 60250 |
0.10 | 0.10 | Conditioned; IEC 60250 | |
Comparative Tracking Index | 475 V | 475 V | DAM; IEC 60112 |
575 V | 575 V | Conditioned; IEC 60112 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
Drying Temperature | 80.0 °C | 176 °F | |
Moisture Content | <= 0.20 % | <= 0.20 % |