Polymer Property : Flexural Strength = 140 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	140 MPa	20300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C4210HF PC+ABS PC+ABS Blend with 10% Glass Reinforce. High flow, High heat resistance., Excellent balance strength/rigidity. Good impact/appearance.
Flexural Strength	<= 140 MPa	<= 20300 psi	ISO 178
Polykemi AB POLYsan FL100 F20 SAN, Glass Fiber-Reinforced Information provided by Polykemi AB
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	Injection; ISO 178
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Flexural Strength	140 MPa	20300 psi	ISO 178
NOVA Chemicals Dylark® 378P30 Glass Reinforced Engineering Resin Features: Ultra high modulus, High heat resistance, excellent adhesion to urethaneApplications: Instrument panel substrates, Brackets, Structural components
Flexural Strength	140 MPa	20300 psi	2.6 mm/min; ASTM D790
PTS PPE-LXS 314-20 PPE-HIPS, 20% Glass Filled Typical Applications: Water industrial partsInformation provided by PTS LLC.
Flexural Strength	140 MPa	20300 psi	2 mm/min; ISO 178
Hexion Bakelite™ PF 6506 Phenolic Formaldehyde Resin, Low Shrinkage, Resistant to High Temperatures, UL Listed &nbs Phenolic molding compound, inorganically filled, glass fiber reinforced, high dimensional stability at raised temperature, good media resistance, heat-resistant, UL listed molding compound 1.5 mm/V-..
Flexural Strength	140 MPa	20300 psi
Lehmann & Voss LUVOCOMÂ® 1105-8432 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect..
Flexural Strength	140 MPa	20300 psi
Lehmann & Voss LUVOCOMÂ® 6-8395 Polyamide 12, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Especially suitable at dynamic stress situations.Electrically conductive, s..
Flexural Strength	140 MPa	20300 psi
Fibre Glast 1110 L Vinyl Ester Resin (Laminate Properties) #1110 is a low viscosity, corrosion resistant vinyl ester resin. It is formulated for maximum corrosion resistance to most fuels, vapors, and both acidic and basic chemicals. It is also heat resista..
Flexural Strength	140 MPa	20300 psi
Lehmann & Voss LUVOCOMÂ® 1106-7223 Polyether imide, with PTFE Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le..
Flexural Strength	140 MPa @Temperature 22.0 Â°C	20300 psi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 2400 Unsaturated Polyester UP SMC 2400 is a SMC with fire retardancy. The glass level has been selected to combine mouldability with strength and stiffness properties. The fire retardancy is especially high, and the material is ..
Flexural Strength	140 MPa	20300 psi	ISO 178
Solvay Specialty Polymers RytonÂ® QA200P Polyphenylene Sulfide (PPS) RytonÂ® QA200P (pelletized) unfilled polyphenylene sulfide exhibits excellent thermal stability and chemical resistance and may be used in injection molding processes.Features: Good Chemical Resis..
Flexural Strength	140 MPa	20300 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP BF004 SAN (Asia Pacific) LNP* Thermocomp* BF004 is a compound based on Styrene Acrylonitrile resin containing Glass Fiber.
Flexural Strength	140 MPa	20300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WFB44 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WFB44 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Glass Bead.
Flexural Strength	140 MPa	20300 psi	ISO 178
Polyram PlusTek PA108 Nylon6/6.6 Alloy for Injection Molding Good surface finish Nylon 6/6.6 alloy for injection molding.Information provided by Polyram.
Flexural Strength	140 MPa	20300 psi	ISO 178-93
Wellman Wellamid® MR410 22H-GY1 40% Mineral Reinforced Nylon 66 Description: Mineral Reinforced Nylon 66Information provided by Wellman.
Flexural Strength	140 MPa	20300 psi	D790
Zhejiang Juner 301-G15 15% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, ..
Flexural Strength	140 MPa	20300 psi	ASTM D790
Unitika M2350 PA6, Dry Nano composite nylonInformation provided by Unitika Ltd.
Flexural Strength	140 MPa	20300 psi	ASTM D790
Polyram PlusTek PD300G4 Nylon 12, 20% Glass Fiber 20% glass-fiber reinforced polyamide 12 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	140 MPa	20300 psi	ISO 178
Polyram RamOfin PPH308G50 Polypropylene, 50% Glass Fiber, Impact Modified 50% Glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applications.Information provided by Polyram.
Flexural Strength	140 MPa @Treatment Temp. 20.0 °C, Time 3600 sec	20300 psi @Treatment Temp. 68.0 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets Description: Electrical and electrotechnical applications. Suitable as high-frequency insulation on account of its dielectric loss. Used as, among other things, an insulation material in large induc..
Flexural Strength	140 MPa	20300 psi	2 mm/min; ISO 178
Eurostar Staramide PF003IX1 PA6, Glass Fiber Filled, Impact Modified, Injection Molded Staramide PF003IX1 is an Impact Modified, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as PF1003HI005)Information provided by Eurostar.
Flexural Strength	140 MPa	20300 psi	2 mm/min; ISO 178
Eurostar Staramide PFB42U PA6, Glass Fiber/Bead Filled, Injection Molded Starflam PFB42U is an UV Stabilized, Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	140 MPa	20300 psi	dry; ISO 178
Azoty Tarnow™ Tarnamid® T-27 GF15 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 15% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..
Flexural Strength	140 - 180 MPa	20300 - 26100 psi	At Rupture; ISO 178
Vyncolit X682 Novolac Phenolic Glass fiber, glass bead and graphite filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction.USES: Water pump seals and self-lubricating bearings.Info..
Flexural Strength	140 MPa	20300 psi	ASTM D790
SABIC Innovative Plastics Lexan® ML3260 PC (Asia Pacific)
Flexural Strength	140 MPa	20300 psi
Lehmann & Voss LUVOCOM® 1200-7116-2 ABS, with carbon fiber Applications: Office communication.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff ..
Flexural Strength	140 MPa	20300 psi	DAM; ISO 178
Solvay Technyl® A 402 H1 Nylon 66 Unreinforced, very high viscosity, heat stabilized, for extrusion and injection molding. TECHNYL® A 402 H1 offers three main advantages: high impact resistance at low humidity levels, good rigidit..