- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 167 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 167 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
|
Nylene® 454 Nylon 6, 50% RH
Injection molding grade. Nylene 454 is the heat stabilized version of 451 recommended for molding applications requiring both maximum durability and toughness. Exceptional fatigue and wear resistanc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYabs R00 ABS, High Impact
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Geloy XTWE265 ASA
Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
|
North Wood Plastics PS with 20% Wood Fiber
Data provided by North Wood Plastics, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP COLORCOMP R1000S PA 66
LNP COLORCOMP* R1000S is an unfilled Nylon 66. Added features of this material is: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
|
LATI LATISTAT 30/R-05 High Impact Strength Polystyrene Base Conductive Plastic
(discontinued **)
Description: Latistat materials have low specific resistivity. They feature partial electrical conductivity. Selected functional additives give materials with low specific resistivity and reasonable..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DIN 53461; ASTM D648 |
|
Kolon KOPA® KN333HI2 High Impact Nylon 66
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
|
LATI Latilub 62-06GR PA6, Graphite Reinforced
Self-lubricating product based on Polyamide 6 (PA6). Graphite. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplast..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
|
LATI Latishield 66-10A PA66, Steel Fiber Reinforced
EMI shielding product based on Polyamide 66 (PA66). Steel fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
75.0
°C <br>@Thickness 3.20 mm
|
167
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Xenoy® IQ1103R PBT+PC (Europe-Africa-Middle East)
Xenoy* Resin iQ1103R - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103R is an unreinforced, impact modified PC + iQ-PBT alloy with excellent low temperature im..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
75.0
°C <br>@Thickness 3.20 mm
|
167
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Asia Pacific)
Transparent, US Food Contact compliant, chemically resistant.
This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require b..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
|
Shinil Chemical SHINSTRA PA-66 W100SRB Structural Polymer Abrasion Resistance
SHINSTRA is the product line of structural polymer compound which exhibits excellent physical, mechanical, and thermal properties. Shinil uses the state-of-the-art dispersion and blending technolog..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 |
|
Styrolution PS 116 N/L GPPS
Styrolution PS 116N/L is a general purpose polystyrene grade with excellent flow properties and improved heat resistance.Excellent flow propertiesHigh heat resistanceInformation provided by Styrolut..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics NORYL PX2245 PPE+HIPS (Europe-Africa-Middle East)
NORYL PX2245 is a halogen free (according to VDE/DIN 472 part815) flame retardant material. The material fulfills the IEC 65 part 20.2 requirement at 1.6 mm thickness.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
75.0
°C <br>@Thickness 3.20 mm
|
167
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® V3900WX PBT+PC
PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
75.0
°C <br>@Thickness 3.20 mm
|
167
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL EXNL1117 PPE+HIPS
high gloss Noryl
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
|
TPI Porene® ABS-AN450 Flame Retardant ABS Resin
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Unannealed; ASTM D648 |
|
Chase Plastics CP Pryme® NN300HL (Dry) Nylon 66, Heat Stabilized, Lubricated
Features: General purposeHeat stabilizedLubricatedForm: PelletsInformation provided by Chase Plastics.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
75.0
°C <br>@Thickness 3.20 mm
|
167
°F <br>@Thickness 0.126 in
|
ASTM D648 |
|
A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
|
Eastman Tenite Propionate 383A2R30012 Natural, Trsp Cellulose Acetate Propionate
Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6600 HWUVCP Nylon 66, UV Stabilized, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
|
Diamond Polymers ABS 9301
Description: Extrusion Grade, Low GlossInformation provided by Diamond Polymers, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
|
E-Polymers TEKAMID® H24WC High Toughness Heat Strength PA/ABS Alloy
Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.H-series: PA6/ABS, PA66/AB..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
|
Aclo Accutech Polypropylene Homopolymer HP0336W30L1 Wollastonite Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 |
|
BASF Ultramid® A4H PA66 (Dry)
Description: Highly heat aging resistant, medium-viscosity injection-molding grade for highly stressed parts such as bearing cages, gearwheels, spool bodies and chain drive tensioners.Information pr..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO data |
|
BASF Capron® 8202C HS Nylon 6 (Dry)
(discontinued **)
Capron 8202C HS is a heat stabilized, low viscosity, polyamide 6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It i..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPH T20040 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPH T5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Unannealed; ISO 75-2/A |
|
Ascend Performance Materials Vydyne® ECO366 Nylon 66, Flame-retardant, DAM
Vydyne® ECO366 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for machin..
|
|||