- Solvay TECHNYL® B 218 Black 21 N PA66/6, DRY
Solvay TECHNYL® B 218 Black 21 N PA66/6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® B 218 Black 21 N PA66/6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced copolyamide PA 66/6 , heat stabilized , medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® B 218 offers all of the primary properties of unreinforced polyamide 66 .In addition , it has improved resistance to high temperature , and can be used for components which will withstand long-term temperature stresses , such as: Automotive industry- diagnostic plugs, ashtray bodies and covers. Electrical industry- housings, connectors, terminal blocks . This product is available in natural, black and grey.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.6 % @Temperature 23.0 °C, Time 86400 sec |
1.6 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 type 1 A |
| Elongation at Break | 30 % | 30 % | ISO 527 Type 1A |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 Type 1A |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 242 °C | 468 °F | ISO 11357 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 |
| Comparative Tracking Index | 425 V | 425 V | Solution B; IEC 60112 |
| 525 V | 525 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 240 - 250 °C | 464 - 482 °F | |
| Front Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 250-260°C |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Rynite® RE19051 BK507 PET (Unverified Data**)
- Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes
- Solvay Chemicals Trifluoroacetic acid methyl ester
- Solvay MACKAM® 2CSF-40CG Surfactant
- ExxonMobil PP143KNE1 Polypropylene Homopolymer
- Clariant Renol PA113G33HR Nylon 66, 33% Glass Fiber, Heat Stabilized, Hydrolysis Resistant
- Asahi Kasei Thermylene® P6-30FG-0699 30% Glass Fiber Reinforced, Heat Stabilized
- Aleris AA5024-H116 Aluminum Magnesium Scandium Alloy
- ATI Allvac® 3-2.5 Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Copyright © lookpolymers.com All Rights Reserved