Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Provisional datasheet - Product in developmentDescription: Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 218HP V30 BLACK 21N offers an outstanding long term heat resistance and is suitable to work in environments characterized by a very high temperature. Offering an excellent combination between thermal and mechanical properties, it is used in all sectors of industry, such as in the automotive for engine components and in the electrical field for bobbin coil.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm | 0.0085 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 Type 1A |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 Type 1A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 Type 1A |
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Charpy Impact Unnotched | 7.80 J/cm² | 37.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.12 % | <= 0.12 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG34LGHF ABS
- Radici Radilon® S 38M (dry) Nylon 6
- Momentive Performance Materials Siloprenâ„¢ LSR 2345/07 Liquid Silicone Rubber - Specialty Coating
- Spartech Royalite R87/59 ABS/PVC Weather Resistant Sheet
- Teknor Apex TruVis Esters™ TOTM TriOctyl Trimellitate
- A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene
- Chosun Refractories MIX-3 Light-Weight Gunning Castable
- Adamas Adalon® 436 PTFE, 15% Ekonol®
- Asahi Kasei Thermylene® P1-35FM-Y942 35% Glass Fiber/Mineral Reinforced
- EVALCA EVAL® EF-XL Ethylene Vinyl Alcohol Copolymer Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved