DuPont™ Dartek® B-602 Nylon 6,6 Barrier Film, 38 µm Thickness, PVDC Coated  (discontinued **)

Category Polymer , Film , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Dartek® B-602 Nylon 6,6 Barrier Film, 38 µm Thickness, PVDC Coated  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.A strong, transparent nylon 6,6 film which has a PVDC coating applied to one side for enhanced barrier to oxygen, moisture, grease and odor. It is specially formulated for use in high humidity applications. Can be printed, laminated, or extrusion coated. In converter combinations, it can be used for any packaging or industrial end use requiring high barrier properties. It can be easily thermoformed for assorted shapes and products such as meats and cheeses.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
Moisture Vapor Transmission 0.340 cc-mm/m²-24hr-atm

@Temperature 38.0 °C
0.864 cc-mil/100 in²-24hr-atm

@Temperature 100 °F
90% RH; ASTM F-372
Water Vapor Transmission 9.00 g/m²/day

@Temperature 38.0 °C
0.580 g/100 in²/day

@Temperature 100 °F
90% RH; ASTM F-372
Oxygen Transmission 0.290 cc-mm/m²-24hr-atm
0.737 cc-mil/100 in²-24hr-atm
or 7.7 cc/m²-24hr-atm for the film at 23°C, 0% RH. ASTM D1434-66
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 300 %
300 %
ASTM D882-64T
Film Elongation at Break, TD 300 %
300 %
ASTM D882-64T
Secant Modulus, MD 0.690 GPa
100 ksi
ASTM D882
Secant Modulus, TD 0.690 GPa
100 ksi
ASTM D882
Coefficient of Friction, Dynamic 0.45
0.45
film to coating; ASTM D1894-63
Elmendorf Tear Strength, MD 1.40 g/micron
35.6 g/mil
ASTM D1922-67
Elmendorf Tear Strength, TD 1.20 g/micron
30.5 g/mil
ASTM D1922-67
Dart Drop Test 600 g
1.32 lb
Impact Strength, ASTM D1709-62T
Film Tensile Strength at Break, MD 70.0 MPa
10200 psi
ASTM D882
Film Tensile Strength at Break, TD 70.0 MPa
10200 psi
ASTM D882
Optical Properties Metric English Comments
Haze 1.5 %
1.5 %
Gloss 150 %
150 %
Transmission, Visible 90 %
90 %
transparent; thickness not quantified